Measurement of Absorption Coeffici eats in Infrared Window Materials by CO<SUB>2</SUB> Laser Calorirnetry
スポンサーリンク
概要
- 論文の詳細を見る
The infrared absorption in widnow materials such as NaCI, KBr, and Kul, which are commercially availanle in Japan, has been studied by means of thecalorimetric technique with a step-tunable CW CO<SUB>2</SUB> maser. The absorptlon coeficientat10.6μm of NaCl is measured to be 2.5×10<SUP>-3</SUP> cm<SUP>-1</SUP>, which is almost twice of theintrinsic multiphonnn absorption. KCI material has the10.6μ m absorption coefficientof 6×10<SUP>-4</SUP> cm<SUP>-1</SUP>, which is about one ordex higher than the intrinsic multiphononabsorption coefficient of 7×10<SUP>-5</SUP> cm<SUP>-1</SUP>. For KBr, the absorption coefficient at 10.6μ mis 1×10<SUP>-3</SUP> cm<SUP>-1</SUP>, which is about four order higher than the intrinsic multiphononabsorption of 2×10<SUP>-7</SUP> cm<SUP>-1</SUP>. (One absorption band at 9.29 μm is observed ln KBr) Three different techniques are tried to separate out bulk and surface absorption.This calorimetric technique is used to obtain the dependence of absorption coefficienton the sample's position in an NaCI ingot.
- 社団法人 レーザー学会の論文
社団法人 レーザー学会 | 論文
- Possible Isotope Separation by a Process of Nuclear Excitation by Electron Transition
- Integrated Optic Flow Meter with Cantilever Structure on Silicon Substrate.
- タイトル無し
- Application of Tunable Vacuum-Ultraviolet Laser to Chemical Reaction Dynamics.
- タイトル無し