Automatic Rapid Growth of Nonlinear Optic Crystal KDP.
スポンサーリンク
概要
- 論文の詳細を見る
The automatic and rapid crystal growth method was developed for water-soluble crystal, KDP. Theover-heating of the water solution of crystal enlarges the metastable zone during the temperature reducingprocess as a result of eliminating an initial cluster density. The higher level of supersaturation up to 200% onKDP crystal was achieved resulting in an average growth rate of 54 mm/day at supersaturation of 38%. Theconcentration of the growth solution was measured by the conductivity of the solution. The supersaturationwas controlled with the dependency of conductivity on temperature by the computer. The 60-mm class KDP single crystal was grown automatically by the method with an average growth rate of 30 mm/day. The spectraltransmittance and laser damage threshold of the rapidly grown crystals were measured. The lower laserdamage threshold of the rapidly grown crystal was improved completely by a thermal conditioning to be 17J/cm<SUP>2</SUP> of 1 ns pulse at 1-μm wavelength.
- 社団法人 レーザー学会の論文
社団法人 レーザー学会 | 論文
- Possible Isotope Separation by a Process of Nuclear Excitation by Electron Transition
- Integrated Optic Flow Meter with Cantilever Structure on Silicon Substrate.
- タイトル無し
- Application of Tunable Vacuum-Ultraviolet Laser to Chemical Reaction Dynamics.
- タイトル無し