Si, Ga As and Al surfaces exposed to etching gases under Ar F excimer-laser (193nm) irradiation have been studied by in situ x-ray photoelectron spectroscopy (XPS). The kinetics of photochemical etching and the resulting products on the solid surfaces have been revealed from the chemical shifts of adsorbates and substrate atoms. The etch products are shown to be Si Fx (x=∼4) units and molecular fluorine in Si etching in NF<SUB>3</SUB>, GaCl<SUB>3</SUB> and AsCl<SUB>3</SUB> in Ga As etching in HCl, and Al Clx (x=2, 3) in an Al/BCl<SUB>3</SUB> system. The valence band spectra of etched Si surface indicate a systematic shift of the band edge to form a surface depletion layers, which is caused by the photogenerated majority carriers trapped in the semiinsulating fluorosilyl surface layer. By controlling the surface chemistry, pattern projection etching and CVD have been achieved.
- 社団法人 レーザー学会の論文
社団法人 レーザー学会 | 論文
- Possible Isotope Separation by a Process of Nuclear Excitation by Electron Transition
- Integrated Optic Flow Meter with Cantilever Structure on Silicon Substrate.
- タイトル無し
- Application of Tunable Vacuum-Ultraviolet Laser to Chemical Reaction Dynamics.
- タイトル無し