Effect of Yttrium Addition on Mechanical Properties for V-4Cr-4Ti Alloy Contaminated with Oxygen and Nitrogen Impurities
スポンサーリンク
概要
- 論文の詳細を見る
Reduction of interstitial impurities such as nitrogen (N) and oxygen (O) improves the mechanical properties of V-4Cr-4Ti alloys. Yttrium (Y) addition effectively reduces O content by Y2O3 slag-out on the melting ingot surface. The effects of Y addition on mechanical properties were investigated for V-4Cr-4Ti with N ranging from 0.009 to 0.29 mass% and O ranging from 0.009 to 0.36 mass%. The increase in yield stress (YS) and ultimate tensile stress (UTS) for vanadium alloys was saturated above 0.1 mass% in O content, because Ti precipitates increased with increasing O content regardless of Y addition. Y addition had little effect on YS and UTS of V-4Cr-4Ti alloys at room temperature (RT). However, Y addition improved impact properties of alloys highly doped with O. Y addition did not suppress hardening due to O doping but did increase deformation for crack initiation.
- 社団法人 プラズマ・核融合学会の論文
社団法人 プラズマ・核融合学会 | 論文
- 磁場中プラズマの中に入れた円柱プラズマのダイポール振動
- 電子共鳴加熱, および同軸銃によるプラズマの高周波パワーの吸収
- 不安定発展における非線形効果 : 秩序形成とカオス
- Fabry-Perot干渉計による電子サイクロトロン輻射の測定法とWT-III トカマクにおける実験結果
- Tritium Inventory in Fusion Machine and Air Detritiation after Accidental Release