Residual Stress Improvement of Nickel Base Superalloy Alloy 706 by Laser Peening

スポンサーリンク

概要

• 論文の詳細を見る

• Some cracks were found at the first stage discs of gas turbine rotors made of Ni-base superalloy. There were inter-granular cracking and observed to be highly stressed and damage sensitive locations with less potential for oxidation, which is thought to occur due to hold-time cracking. In this study, laser peening technology was developed to improve fatigue properties of Ni-base superalloy Alloy 706, and the effects on the material properties were examined. Laser peening is a novel process to induce compressive residual stress on material surface by irradiating focused high-power laser pulses. Several durability tests, such as thermal aging treatment test and stress aging test, were performed under thermal power plant operation conditions, and the effectiveness of laser peening treatment was confirmed.

著者

• 宮部 正道

  中部電力（株）

• 鍵谷 幸生

  中部電力（株）

• 小林 大輔

  中部電力（株）　技術開発本部　電力技術研究所

• 吉岡 洋明

  （株）東芝

• 伊藤 明洋

  中部電力（株）

• 千田 格

  （株）東芝

• 角谷 利恵

  （株）東芝

• 斎藤 大蔵

  （株）東芝

• 澤 徹

  （株）東芝

関連論文

• 火力発電プラントで使用された高温再熱蒸気管用改良9Cr-1Mo鋼エルボ管の損傷評価
• 再生熱処理によるNi基超合金の曲げ荷重下でのクリープ損傷回復
• 三次元ハイブリッドサンプリングモアレ法による構造物の応力集中評価
• 原子力プラントのレーザ溶接技術に関する研究
• Residual Stress Improvement of Nickel Base Superalloy Alloy 706 by Laser Peening
• 実機環境下における腐食ピット損傷評価に基づくガスタービン圧縮機翼の腐食疲労寿命予測

スポンサーリンク