高温酸化スケールのブリスタリングの成長過程に及ぼす窒素の影響

概要

論文の詳細を見る
Blistering occurs when oxide scale swells during oxidation at high temperatures. Blistered scale causes surface defects when rolled. The present study investigated the effect of nitrogen on blister growth when steel is oxidized at high temperatures, and drew the following conclusions. Atmospheric conditions before oxidation affect blister growth. Blisters nucleate but do not grow, when a steel sample is held in Ar gas or in vacuum before oxidation. Blisters inflate when a steel sample is held in N2 gas before oxidation. The gas inside the grown blisters is mainly N2 gas. The steel surface is nitrided in N2 gas at high temperatures. It is deduced that the steel surface is nitrided before oxidation, and the nitrogen component causes blister growth upon its release as N2 gas at the scale/steel interface.