Fracture of Notched GF/PP Plates in Dynamic Tensile Strength Test
スポンサーリンク
概要
- 論文の詳細を見る
The effects of notch geometry on the tensile strength of notched fiber-reinforced polymer (FRP) plates in dynamic tensile strength tests were investigated. A short-glass-fiber-reinforced polypropylene (GF/PP) plate containing 30% E-glass fiber by weight was prepared by injection molding. The notch-root radii were 0.5, 1, and 2mm, while the notch depth ranged from 2 to 5mm. Dynamic tensile strength tests were carried out at room temperature of 23°C and a tensile speed of 1000mm/s. The validity of the fracture criterion based on the concept of the severity near the notch root was previously confirmed for notched FRP plates under static loading. In other words, the maximum elastic stress at fracture is determined only by the notch-root radius. This is accomplished by the experimental data of the static tensile test at a constant cross-head speed of 0.5mm/min (= 0.008mm/s). When the time to a fracture was the same, the results of the dynamic tensile strength tests showed that the maximum elastic stress at fracture is determined by the notch-root radius but is independent of the notch depth. Thus, the concept of the severity near the notch root could be applicable to the fracture of notched FRP plates in dynamic tensile tests. On the other hand, the fracture strength of FRP is time-dependent, and this dependence is called viscoelastic behavior. Therefore, when the tensile speed is varied, the maximum elastic stress at fracture would be determined by the notch-root radius and time.
著者
関連論文
- 繊維強化ポリカーボネート切欠平板の疲労破損の条件(破壊力学)
- ガラス繊維強化ポリカーボネート切欠平板の静的破壊特性
- ポリカーボネート平滑試験片における疲労き裂の発生と進展
- 切欠きをもつGF/PPの強度および破壊挙動に及ぼす温度とリサイクルの影響
- 鈍くて浅い切欠きをもつFRP板の静荷重による破壊
- 切欠きをもつFRP板の静荷重による損傷 : 輝度測定法による損傷評価
- 切欠きをもつGF/PP射出成形板の強度および損傷に及ぼす繊維長さの影響
- 輝度測定によるFRP切欠平板の静荷重のもとでの損傷の検出と評価
- FRP切欠平板の静荷重のもとでの破壊過程とAE特性
- 引張りおよび曲げを受ける直交異方性切欠平板の切欠底付近における応力分布
- 一方向CFRP積層板の曲げによる静的, クリープおよび疲労の破壊挙動の時間および温度依存性
- 切欠きをもつFRPの疲労破損の条件
- FRPリサイクル材の強度に関する基礎的研究 : 射出成形板の強度に及ぼす繊維含有率の影響
- 切欠きをもつFRP板の静的破壊特性に及ぼす切欠形状と繊維方向の影響(高分子系複合材料)
- FRP切欠試験片の疲労破損に及ぼす切欠深さの影響
- 円孔をもつFRP板の引張りによる破壊の条件
- FRP切欠試験片の疲労損傷に及ぼす切欠半径の影響
- ガラス繊維強化ポリカーボネートにおける樹脂/繊維界面の損傷挙動と改質効果の関係
- 端部切欠きをもつ一方向不連続繊維強化プラスチックの破壊基準
- 樹脂/繊維界面を改質したGFPCにおける疲労強度特性と損傷機構の関係
- Fracture of Notched GF/PP Plates in Dynamic Tensile Strength Test