Dynamic Transformation Behavior of a Deformed High Carbon Steel at Temperatures Above the Ae3
スポンサーリンク
概要
- 論文の詳細を見る
The dynamic transformation behavior of deformed austenite was studied in a 0.79%C high carbon steel over the temperature range 743–823°C. The experiments were carried out in torsion under an atmosphere of argon and 5% H2. All these temperatures are above the orthoequilibrium Ae3 temperature of the steel. Strains of 0.25–4 were applied at a strain rate of 4 s–1. The experimental parameters were varied in order to determine the effects of strain and temperature on the formation of strain-induced ferrite and cementite. The critical strain for dynamic transformation was about 0.20. The volume fractions of the transformed phases increased with strain and decreased with temperature. The observed ferrite structures are Widmanstätten in nature and appear to have formed displacively. The carbon diffusion times required for formation of the observed spheroidal cementite particles were calculated; these are consistent with the occurrence of interstitial diffusion during deformation. Similar calculations indicate that substitutional diffusion does not play a role during dynamic transformation.
- The Iron and Steel Institute of Japanの論文
著者
-
Jonas John
Department Of Materials Engineering Mcgill University
-
Basabe Vladimir
Department Of Metals And Materials Engineering Mcgill University
-
Ghosh Chiradeep
Department of Materials Engineering, McGill University
-
Yue Stephen
Department of Materials Engineering, McGill University
-
Xiong Xiang
Monash Centre for Electron Microscopy and Department of Materials Engineering, Monash University
-
Basabe Vladimir
Department of Materials Engineering, McGill University
関連論文
- The Dynamic, Static and Metadynamic Recrystallization of a Nb-microalloyed Steel
- Effect of Chromium, Boron and Manganese Additions on the Deformation and Recrystallization Textures of Warm Rolled Low Carbon Steels
- The Deformation Microstructure and Recrystallization Behavior of Warm Rolled Steels
- Effect of alloying elements on the microstructure and texture of warm rolled steels
- Correlation between the Deformation and Post-deformation Softening Behaviours in Hot Worked Austenite
- Effect of Processing Schedule on the Microstructure and Texture of 0.78wt% Cr Extra-low-carbon Steel
- The Formation of Deformatio Induced Ferrite during Mechanical Testing
- Predicting the Critical Stress for Initiation of Dynamic Recrystallization
- Softening and Flow Stress Behaviour of Nb Microalloyed Steels during Hot Rolling Simulation
- Evaluation of the Hot Ductility of a C-Mn Steel Produced from Scrap Recycling
- Effect of Microstructure on the Cold Headability of a Medium Carbon Steel
- Design of Microalloyed Steel Hot Rolling Schedules by Torsion Testing : Average Schedule vs. Real Schedule
- The Ferrite Transformation in Hot Deformed 0.036% Nb Austenite at Temperatures Above the Ae_3
- AIN Precipitation in Dual-phase 3% Si Electrical Steels
- The Hot Strip Mill as an Experimental Tool
- Effect of Finishing Temperature on Hot Band Textures in an IF Steel
- Effect of Silicon on the Kinetics of Nb(C, N)Precipitation during the Hot Working of Nb-bearing Steels
- Growth Rate and Phase Composition of Oxide Scales during Hot Rolling of Low Carbon Steel
- Effect of O_2 in Heating Atmosphere on Hydraulic Descaling in Hot Rolling of Low Carbon Steel
- Dynamic Transformation of a Low Carbon Steel at Temperatures above the Ae_3
- The Critical Strain for Dynamic Transformation in Hot Deformed Austenite
- Dynamic Transformation Behavior of a Deformed High Carbon Steel at Temperatures Above the Ae3
- Effect of Intercritical Heat Treatment on the Microstructure and Mechanical Properties of Medium Mn Steels
- The Critical Strain for Dynamic Transformation in Hot Deformed Austenite