Oxide Ion Conduction in the Perovskite-type LaYO3 Doped with ZrO2
スポンサーリンク
概要
- 論文の詳細を見る
In order to find a new type of oxide ion conductor, the electrical conduction was measured in the substituted perovskite-type oxides. In the present case, LaYO3 was used as a based material with an orthorhombic and comparatively large unit cell, and a novel substitution method was introduced to intend to increase the concentration of oxide ions, e.g., LaY1−xZrxO3+x/2. As a result, the LaYO3-based perovskite-type solid solution was found to be formed, where the enhanced oxide ion conduction was observed as compared with that of the based material. A typical sample was LaY0.95Zr0.05O3.025, the ionic conduction of which was 1.2×10−2 S cm−1 at 1000°C. Another substitution method of La1−xZrxYO3+x/2 resulted in the analogous result. Considering these results and the further structural and density measurements, the charge carriers in these phases were expected to be due to interstitial oxide ions.
- 公益社団法人 電気化学会の論文
著者
-
ESAKA Takao
Department of Chemistry & Biotechnology, Graduate School of Engineering, Tottori University
-
Binti Che
Department of Chemistry & Biotechnology, Graduate School of Engineering, Tottori University
関連論文
- 灰重石型およびスピネル型酸化物固溶体の特異な酸化物イオン伝導性
- リチウム貯蔵性金属間化合物Mg2Geの局所構造
- Synthesis of Lithium Storage Intermetallic Compounds as Anode Materials
- Neutron Diffraction Study on the Defect Structure of Ta-Substituted Zn_2TiO_4 Oxide Ion Conductors
- Defects and oxide ion transport properties in the substituted Zn2TiO4
- Defect structure of Ta- and Al- doped Zn_2TiO_4 showing oxide ion conduction via cation vacancy
- 冷中性子ラジオグラフィ-を用いたLi1.33Ti1.67O4中のリチウムイオンの動きの解析
- 中性子ラジオグラフィによるリチウム電池内におけるリチウム元素分布の可視化〔英文〕
- メカニカルアロイングによるBi2O3を母体とした蛍石型の固溶体の調製
- (Bi2O3)0.80(Nb2O5)0.20 のメカニカルアロイングにおける形態観察
- Neutron Diffraction Study on the Defect Structure of Ta-Substituted Zn2TiO4 Oxide Ion Conductors
- Ca0.9Nd0.1-yMnO3-δ型ペロブスカイト酸化物焼結体の調製とそのアルカリ溶液中での電池正極活物質としての性質
- LiBaF3-xHxの合成とイオン伝導性
- イオン-電子混合伝導体の熱起電力測定
- 高電子伝導性セラミックCa0.9La0.1MnO3-δの中性溶液中での電池正極特性
- Conduction Property of PbWO_4- and PbMoO_4-based Oxide Ion Conductors in Lower Oxygen Partial Pressures
- Cathode Performance of LiMn2O4 Thick Films Prepared by Gas-Deposition for Lithium Rechargeable Battery
- Oxide Ion Conduction in the Perovskite-type LaYO3 Doped with ZrO2