アルカリ性溶液中におけるPtPb, PtBi及びPtBi金属間化合物のエタノール,メタノール電極触媒酸化活性
スポンサーリンク
概要
- 論文の詳細を見る
The electrocatalytic activities of a wide range of intermetallic bulk compounds in the ethanol (EtOH) and methanol (MeOH) oxidation reactions in alkaline media have been studied, and the results have been compared to those of pure polycrystalline Pt and Pd electrodes. The PtPb, PtBi, and PtBi2 intermetallic compounds appeared to be the most promising electrocatalysts among all of the examined bulk electrodes. The current densities at −0.2 V (vs. Ag/AgCl KCl satd.) for PtPb, PtBi, and PtBi2 in EtOH were 21.4, 7.73, and 6.03 mA cm−2, respectively. All of the other intermetallic bulk electrodes exhibited current densities less than 2.5 mA cm−2. PtPb had the lowest onset potential of −0.58 V for EtOH oxidation, which was 20–30 mV less than that of pure Pt and Pd. The current densities of PtPb were at least seventeen times larger than those of pure Pt and Pd. PtBi and PtBi2, which have onset potentials of −0.51 and −0.45 V, respectively, for the EtOH oxidation reaction exhibited extremely stable oxidation currents of 4.8 and 3.3 mA cm−2 during the constant-potential electrolysis of EtOH. The same behavior was also observed for the MeOH oxidation with PtPb, PtBi, and PtBi2 intermetallic compounds.
著者
-
Matsumoto Futoshi
Department Of Applied Chemistry Tokyo Metropolitan University
-
MATSUMOTO Futoshi
Department of Material and Life Chemistry, Faculty of Engineering, Kanagawa University
関連論文
- Electrochemical Energy Generation and Storage : Fuel Cells and Lithium-Ion Batteries
- Surface-enhanced Raman Scattering on Ordered Gold Nanodot Arrays Prepared from Anodic Porous Alumina Mask
- チオフェノ-ル修飾金電極による水溶液中でのス-パ-オキシドイオンの電解生成〔英文〕 (バイオエレクトロケミストリ-の新展開)
- Electrochemical Behavior of Graphite-Lithium Intercalation Electrode in AlCl_3-EMIC-LiCl-SOCl_2 Room-Temperature Molten Salt
- 水溶液中におけるポリアニリン修飾電極を用いたスーパーオキシドイオンの電解生成
- Activation of a Li-rich Solid-Solution Layered Li[Ni_Li_Co_Mn_]O_2 Cathode and Retention of High Capacities via an Electrochemical Pretreatment with a Low Discharge Voltage Limit
- アルカリ性溶液中におけるPtPb, PtBi及びPtBi金属間化合物のエタノール,メタノール電極触媒酸化活性
- Relationship between Electrochemical Pre-Treatment and Cycle Performance of a Li-Rich Solid-Solution Layered Li1−α[Ni0.18Li0.20+αCo0.03Mn0.58]O2 Cathode for Li-Ion Secondary Batteries