Comparison of Residual Stress Distributions of Similar and Dissimilar Thick Butt-Weld Plates

概要

論文の詳細を見る
Residual stress distributions of 35 mm thick dissimilar metal butt-weld between A533B ferritic steel and Type 304 austenitic stainless steel (304SS) with Ni alloy welds and similar metal butt-weld of 304SS were measured using neutron diffraction. Effects of differences in thermal expansion coefficients (CTEs) and material strengths on the weld residual stress distributions were discussed by comparison of the residual stress distributions between the similar and dissimilar metal butt-welds. Residual stresses in the similar metal butt-weld exhibited typical distributions found in a thick butt-weld and they were distributed symmetrically on either side of the weld line. Meanwhile, asymmetric residual stress distributions were observed near the root of the dissimilar metal butt-weld, which was caused by differences in CTEs and yield strengths among both parent materials and weld metals. Transverse residual stress distribution of the dissimilar metal butt-weld was similar trend to that of the similar metal butt-weld, since effect of difference in CTEs were negligible, while magnitude of the transverse residual stress near the root depended on the yield strengths of each metal. In contrast, the normal and longitudinal residual stresses in the dissimilar metal butt-weld distributed asymmetrically on either side of weld line due to influence of differences in CTEs.