Low temperature preparation of Ce-TZP/Ba hexaaluminate composites
スポンサーリンク
概要
- 論文の詳細を見る
Composites consisting of Ce-TZP matrix and in-situ grown particles of barium hexaaluminate (BaAl12O19) as the second phase were prepared. To lower the sintering temperature and improve the microstructure of the composites, starting materials of two types of the second phase were used: mixed powders of BaCO3 and α-Al2O3, and amorphous precursor powder. When the composites were prepared using the mixed powder of BaCO3 and larger α-Al2O3 (3.0 µm) particles, aggregations of in-situ formed BaAl12O19 particles were observed in the Ce-TZP matrix. Although the formation temperature of BaAl12O19 decreased with decreasing average size of α-Al2O3 particles, full dense composites were unobtainable, even at the sintering temperature of 1400°C. To lower the formation temperature of the second phase further, amorphous precursor powder of BaAl12O19 was prepared using coprecipitation method. The composite prepared using the amorphous precursor powder was sufficiently densified at 1400°C. The BaAl12O19 particles formed in the composite were finer than those prepared using the mixed powder of BaCO3 and α-Al2O3.
- 公益社団法人 日本セラミックス協会の論文
著者
関連論文
- Microstructure control of Ce-TZP/Ba ferrite composites using an amorphous precursor of the second phase
- Thermal stability improvement of porous alumina prepared from anisotropic boehmite particles
- Fabrication of porous alumina using anisotropic boehmite particles
- Pyroelectricity of Preferably-Oriented Pb_5Ge_Si_xO_ Thick Films Prepared by the Printing Technique : F: FERROELECTRIC MATERIALS
- Kinetics and Mechamism of the High-Temperature Selenidization of Titanium
- Fabrication of BaTiO3/Ag composites using uniform Ag-deposited BaTiO3 particles
- Low Temperature Synthesis of Titania Gel Containing Anatase and Rutile
- Fabrication of Ce-TZP/Ba hexaaluminate composites using amorphous precursor of the second phase
- Low temperature preparation of Ce-TZP/Ba hexaaluminate composites