電析Ni-P合金めっきの熱処理による皮膜構造変化と硬さとの関係
スポンサーリンク
概要
- 論文の詳細を見る
Electroplated Ni-P films with a range of P contents were prepared an electroplating method based on a Watt type bath. Vicker's hardness of each specimen was measured after annealing at 200-800°C. The hardening mechanisms for the Ni-5wt%P and Ni-11wt%P films were studied in detail by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Hardness of the Ni-5wt%P film increased gradually at annealing temperatures up to 400°C and then decreased at higher annealing temperatures. The hardness of the Ni-11wt%P films, on the other hand, showed no increase at annealing temperatures up to 300°C, and a sudden increase at 400°C, with no further change at higher annealing temperatures.The mechanisms of hardening were different for the two films. As-plated Ni-11wt%P film had an amorphous structure, while hardened specimens exhibited the two phase structure of Ni3P-Ni with an Ni3P matrix, and its hardening is attributed to the formation of Ni3P. As-plated 5wt%P film had an f. c. c structure, and the specimens annealed at 400°C showed little structural change except for a gradual increase in the lattice parameter as annealing time increased, indicating that oversaturated P is excluded from the Ni lattice. Given that no Ni3P precipitates were observed, it was concluded that segregation of P to the grain boundaries was the mechanism of hardening. The softening of this film at 800°C was considered to be due to the formation of an Ni-rich structure containing the Ni3P phase.
- 一般社団法人 表面技術協会の論文
著者
関連論文
- TiB_2-ZrO_2-SiC複合材料の微細構造と焼結メカニズム
- 6a-W-8 暗視野像強度の解析によるスピノーダル組成波の定量分析
- ケンブリッヂ大学留学報告
- IV. 気相めっき討論会(第 118 回講演大会討論会報告)
- 24p-Q-12 TEM/PEELSを用いた状態分析
- 3a-TA-5 パラレルEELS分析における検出限界の向上
- アモルファスWO3-TiO2薄膜を用いたEC素子の寿命
- アルミニウムめっき鋼板の耐食性・耐熱性改善におよぼすTi中間層の効果
- Ni-P共晶合金の連続電気めっき
- クロムイオンプレーティング膜の初期結晶成長と膜特性に及ぼす基板前処理の影響(気相めっき)(表面処理)
- Al/Ti2層めっき鋼板の陽極酸化特性
- 電析Ni-P合金めっきの熱処理による皮膜構造変化と硬さとの関係