13Mおよび1.5M硫酸溶液中のAlダイカスト合金ADC12のアノード酸化挙動

概要

論文の詳細を見る
ADC 12 specimens were anodically oxidized in 13M and 1.5M sulfuric acid solutions at constant current densities (ia), and the amounts of oxide film (Woxide), Al3+ions dissolved in the solutions (Wd) and the volume of gas evolved from the anode (Vg) were examined as functions of the anodizing conditions. There was more Wd, less Vg, and more Woxide in the 13M solution than in the 1.5M solution. This suggests that the Al3+ions dissolution current (id) is larger, O2 gas evolution current (ig) is smaller, and oxide formation current (iox=ia-(id+ig)) is larger in the 13M solution than in the 1.5M solution. Since the films formed in the 13M solution had larger values of iox and larger amounts of SO42-ions than the films formed in the 1.5M solution, the film weight, coating ratio, Si content, and thickness were larger for the 13M-films than for the 1.5M-films. Because microvoids were present in both the barrier layer and the porous walls, the hardness of the 13M-films was lower than that of the 1.5M-films.
社団法人表面技術協会の論文