焼結クロムのプラズマ浸炭

概要

論文の詳細を見る
Plasma-carburizing treatment of powder metallurgy chromium was carried out and the following results were obtained.1) X-ray diffraction analysis showed the formation of Cr3C2, Cr7C3 and Cr23C6.2) Cr23C6 was formed in the surface at the early stages of the carburizing process, but Cr7C3 and Cr3C2 were formed as treatment proceeded.3) The thickness of the carbide layer was proportional to the square root of treatment time
社団法人表面技術協会の論文