加圧焼成した炭素製品の異方性

スポンサーリンク

概要

• 論文の詳細を見る

• Graphitized carbon products contain anisotropy in their own properties. Its degree depends on the condition of filler and binder. Soft carbon such as petroleum coke, is used as filler material, and tends to become needlelike particles when crushed. The crystallites of graphite orient along its length. By extrusion, these coke particles line up selectively in the pressing direction, whereby anisotropy grows, and in molding process, those ones line up perpendicularly in the pressing direction.Meanwhile, the product kept under compression during carbonization get shrunk in its own volume, and then it shrinks again in graphitization process. Accordingly, such product results in possessing higher density than usual product.In this investigation, the carbonization under compression, purposed to increase in apparent density of carbon product, was carried out. The orientation of crystallite grown in the sample was estimated from the anisotropy in electrical resistance, thermal expansion, and X-ray diffraction obtained.The following results were obtained:(1) The products from carbonization under compression of mixture of petroleum coke powders and binder possessed more anisotropy than usual molded products. This fact suggests that the compression facilitated the flow of the particles.(2) The samples from the pre-extruded product, carbonized under compression, possessed less anisotropy than usual extruded products. It is considered that the effect of extrusion on orientation and that in molding interacted reciprocally.

• 社団法人 日本材料学会の論文

著者

• 大槻 真一

  大阪工業技術試験所

• 堀 昭二

  大阪工業技術試験所

• 松尾 寛二

  大阪工業技術試験所

関連論文

• 313 熱可塑性プラスチックのざらつき摩耗特性の経年変化(高分子材料)
• 308 ガラス布入エポキシ樹脂積層板の三点曲げ試験における破壊形態とAEの挙動(複合材料II)
• 331 炭素繊維強化プラスチックの衝撃値に及ぼす試験条件の影響(高分子III)
• 層状炭素微粒子を充てんしたエポキシ樹脂の摺動特性
• 321 フッ化グラファイト充てんエポキシ樹脂の摺動特性(高分子I)
• フッ化グラファイト(C2F)nを充てんしたエポキシ樹脂の摺動特性
• 加圧焼成した炭素製品の異方性
• 放電加工用黒鉛電極について
• コールタールピッチの加圧下での炭化について

スポンサーリンク