高炉煉瓦の侵蝕に関する岩石学的研究
スポンサーリンク
概要
- 論文の詳細を見る
Eroded refractory samples removed from the lining of a blast furnace were examined petrographically by means of chemical analysis, microscopic observation, and X-ray powder photography. From the results obtained, it is concluded that the erosive actions on the refractories were to be classified as follows;(a) Erosive action by alkali (especially by potash)Alkali salts, sublimated from ores and fuels, reacted with the refractories used in the stack and the tuyeres level wall, resulting in the formation of alkaline minerals such as kaliophilite, leucite, (K, Na)2CO3, etc. Incongruent melting of mullite also occurred accompanied with this reaction, resulting in the formation of corundum crystals.(b) Erosive action by slagIt is marked that the slag attack against the refractories used in the tuyeres level wall was very severe. Here, calcareous minerals such as melilite, olivine, pyroxene, plagioclase, etc, were produced. Their mineral association seems to have some regularities.(C) Re-crystallization at high temperatureThe refractories used in the hearth were completely re-crystallized, though there was no addition of foreign materials. Corundum crystals, almost absent in the original fire-clay brick, were created and developed through incongruent melting of mullite.(D) Erosive actions by other factorsDisintegration by co is suggested by the presence of carbon in many samples. The formation of Zn compounds, metals, Spinel group minerals, etc, are also noteworthy.
- 社団法人 日本セラミックス協会の論文
著者
関連論文
- MgOとFe_2O_3との反応とそのマグネシアの焼結に対する影響
- 合成コーデイーライトの熱膨張
- 高炉煉瓦の侵蝕に関する岩石学的研究
- 断熱煉瓦の研究
- MgO-Al_2O_3-SiO_2H_2O系研究の進展
- 山口県宇久鉱山産蝋石
- コーディーライト磁器の研究-1-