LEED観察を行ったCu-Pd (001) 合金表面のAESによる組成分析
スポンサーリンク
概要
- 論文の詳細を見る
Many alloy surfaces which have various composition are prepared by depositing palladium to a thickness of 11.7 nm onto (001) surface of copper and subsequent heatings. The surface structure of them is investigated by LEED and the mean surface composition of them is determined using AES data.<BR>After depositing of palladium streak, c (2 × 2) and (1× 1) LEED patterns have been observed with decreasing palladium content. Surface periodicity of the c (2 × 2) structure is in agreement with that of a (001) section of the bulk ordered structure of Cu<SUB>3</SUB>Pd (α).<BR>Enrichment of copper or palladium in the surface of Cu-Pd alloy is shown to be small by analyzing the AES peaks at 60 eV, 770 eV and 840 eV for copper and at 330 eV for palladium.
- 日本真空協会の論文
著者
関連論文
- 24pPSA-38 γ-Mn_3Rh規則相のネール温度の圧力依存性
- 17aZA-2 MnNの異常熱膨張
- 六方晶窒化硼素のX線回折による圧力検定
- 4a-G-16 Fe-Ni合金の磁性と状態図
- 二元共晶型状態図の加圧下における共晶温度の予言と検証
- 24pPSB-59 反強磁性体Mu_3Rh合金の圧縮率とネール温度の圧力依存症
- LEEDによるSi清浄表面へのガス吸着の研究 : X線・粒子線
- Ag-Cu系の高圧力下の状態図
- 合金状態図に対する圧力効果
- Cu-Sn (100) 合金表面のLEED図形観察
- LEED観察を行ったCu-Pd (001) 合金表面のAESによる組成分析
- 低速電子回折法(LEED)によって得られた銅-酸素系表面構造の「酸素圧-熱処理図」
- 6p-L-2 Cu-Pd合金表面の構造(LEED,AES)
- 12a-J-10 CuAu合金表面のLEEDによる観察
- 4a-B-4 Cu(110)面上にAuを蒸着した表面のLEEDによる観察
- LEEDによるSi清浄表面の研究 : X線粒子線
- タイトル無し