The injection molding process (MIM)for the Ti-15Mo-3Al alloys has been studied by using the mixed powder consisting of Ti.Mo and TiAl. The average size of these powders was 38 μm. 1.24μm and 9.4μm, respectively. The results obtained were as follows.<BR>1) The kneading, molding and debinding (in the first stage)processes were successfully performed even in the air.<BR>2) The compacts debound at 210°C in the air, followed by debinding at 500-550°C in a vacuum, were densified to a relative density of 97% or more after sintering for 3 hours at 1296°C in a high vacuum.<BR>3) Many precipitated TiC partic]es were observed in these sintered compacts. which were not observed for the compacts obtained by conventional P/M process.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- SKH51鋼粉の焼結性に及ぼすB粉およびAl2O3粉微量添加の効果 (特集 各種粉末の焼結機構と新しい焼結技術の展開)
- 混合粉の粉末射出成形法により作製した18Ni系マルエージング鋼の焼結と強度に及ぼすTi添加量の影響
- 高速度鋼射出成形体の焼結性および機械的特性に及ぼすBおよびAl_2O_3の微量添加の効果
- SKH51鋼粉の焼結性に及ぼすB粉およびAl_2O_3粉微量添加の効果
- B元素微量添加高速度鋼粉の射出成形
- W-ZrO2系傾斜機能材料の作製
- スラリー減圧法によるSUS440C鋼発泡体の機械的性質
- スラリー減圧法によるNiTiフォームの作製とその形状記憶特性
- スラリー減圧法によるTi発泡体の作製
- 混合粉を用いたマルエージング鋼の作製
- SUS316L鋼粉の焼結性に及ぼすB粉およびAl_2O_3粉微量添加の効果
- Cu焼結体の膨れ防止と強化に及ぼすZrO_2微粉添加の効果
- Ti-12Mo焼結合金のち密化と強度に及ぼすC,Ni,Co粉の微量添加の効果
- Ti-12Mo合金の密度と強度に及ぼす射出成形工程での中間CIP処理の効果
- B元素微量添加SUS316L鋼粉の射出成形
- NiおよびZrの微量添加によるMo粉の活性化焼結
- MIM法で作製したSCM415鋼のC含有量と機械的性質に及ぼす作製条件の影響
- W-Cu混合粉の焼結性に及ぼす原料粉の前処理の影響
- 金属粉射出成形体の焼結性に及ぼす雰囲気の影響
- Ti-Mo-Al混合粉の射出成形 (粉末の成形・加工・評価)
- 円筒形金型を用いた金属粉体圧縮成形過程における半径方向応力について
- W-Cu混合粉の焼結性に及ぼす原料粉の前処理の影響
- Ti-Mo-Al混合粉の射出成形
- 金属粉射出成形体の焼結性に及ぼす雰囲気の影響
- ステンレス鋼粉射出成形の焼結過程における変形について
- Fe-8Ni混合粉射出成形体のバインダー組成が脱脂及び焼結過程に及ぼす影響
- ステンレス粉射出成形体の焼結に及ぼす脱脂状態の影響
- Fe-50%Co混合粉の射出成形
- 金属粉の射出成形・焼結に関する研究(第1報) : Fe粉およびFe-Si混合粉射出成形体の焼結過程に及ぼすシラン処理の効果
- ステンレス粉の射出成形について
- 金属焼結体の高速圧縮変形挙動
- 金属圧粉体の降伏条件
- 噴霧銅粉およびα-アルミナ粉の三軸圧縮成形
- 金属粉体の三軸圧縮試験