パラタングステン酸アンモニウムの熱分解過程
スポンサーリンク
概要
- 論文の詳細を見る
During thermal decomposition of ammonium paratungstate (Monoclinic and Orthorhombic AP T), study on formation process of very fine grain tungsten oxide particle was carried out by thermobalance in nitrogen atmosphere. Thermogravimetric analysis, X-ray diffraction, scanning electron microscopy and specific surface area measurement have been used to make clear the thermal decomposition process. The results obtained are as follows.<BR>(1) Both monoclinic and orthorhombic APT decompose into WO<SUB>3</SUB> through the following order:<BR>5(NH<SUB>4</SUB>)<SUB>2</SUB>O⋅12WO<SUB>3</SUB>⋅5H<SUB>2</SUB>O→X(NH<SUB>4</SUB>)<SUB>2</SUB>O⋅12WO<SUB>3</SUB>→12WO<SUB>3</SUB><BR>5(NH<SUB>4</SUB>)<SUB>2</SUB>O⋅12WO<SUB>3</SUB>⋅11H<SUB>2</SUB>O→X(NH<SUB>4</SUB>)<SUB>2</SUB>O.12WO<SUB>3</SUB>→12WO<SUB>3</SUB><BR>(2) Crystal system of X(NH<SUB>4</SUB>)<SUB>2</SUB>O⋅12WO<SUB>3</SUB> changed along the following step.<BR>APT→Amorphous→Hexagonal ammonium tungsten bronze (→Monoclinic WO<SUB>3</SUB>)<BR>(3) Ultrafine individual particles are formed on the original APT particle changed like spongy at around 773K, and the particles were uniform in size and shape.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- WO_3の直接炭化反応によるナノWC粉末の製造
- 酸化タングステンの水素還元機構
- パラタングステン酸アンモニウムの熱分解におけるアンモニウムタングステンブロンズの生成条件
- パラタングステン酸アンモニウムの熱分解における超微粒タングステン酸化物の生成機構
- パラタングステン酸アンモニウムの熱分解過程
- 超微粒炭化タングステン粉末および超微粒超硬合金の製造技術の開発
- パラタングステン酸アンモニウムの熱分解過程
- パラタングステン酸アンモニウムの熱分解における超微粒タングステン酸化物の生成機構
- パラタングステン酸アンモニウムの熱分解におけるアンモニウムタングステンブロンズの生成条件