Influence of Measuring Method on Young's Modulus and Comparison with Young's Modulus and Mechanical Property of Sintered Irons
スポンサーリンク
概要
- 論文の詳細を見る
In this study, the relationships between porosity and Youngs moduli measured by an acoustic pulse method, a resonance frequency technique, a tensile test and a bending test of sintered irons were investigated. Moreover, tensile strength and proof stress were measured by tensile test, and these values and Youngs modulus were evaluated against porosity.<BR>Youngs moduli measured by the acoustic pulse method, resonance frequency technique and tensile test, except for the bending test, were nearly equal at the same porosity. In the case of the bending test, the moment of inertia of the area was a linear function of porosity. Youngs modulus measured by the bending test, which was corrected by use of the above relation, was equal to that by other method. Youngs modulus measured by the bending test was 0.7-0.8 times of Youngs modulus measured by the tensile test.<BR>Youngs modulus (E), tensile strength (T<SUB>s</SUB>) and proof stress (P<SUB>s</SUB>) against porosity (P) are expressed as E=(E<SUB>0</SUB>-K<SUB>E</SUB>⋅P) (1-P), T<SUB>s</SUB>=(T<SUB>so</SUB>-K<SUB>Ts</SUB>⋅P)(1-P) and P<SUB>s</SUB>=(P<SUB>so</SUB>-K<SUB>ps</SUB>⋅P)(1-P), respectively. Here, E<SUB>0</SUB>, T<SUB>so</SUB> and P<SUB>so</SUB> are Youngs modulus, tensile strength and proof stress at P=0, and K<SUB>E</SUB>, K<SUB>TS</SUB> and K<SUB>PS</SUB> are the experimental coefficients of each relation. Moreover, we found that the relationships among Youngs modulus, tensile strength and proof stress are in positive correlation.
- 社団法人 粉体粉末冶金協会の論文
- 2003-02-15
著者
-
ASAMI Junichi
Tokyo Metropolitan Industrial Technology Center
-
Asami J
Tokyo Metropolitan Industrial Technol. Res. Inst. Tokyo
-
Tanaki T
Tokyo Metropolitan Industrial Technol. Res. Inst. Tokyo
-
Tanaki Toshiyuki
Tokyo Metropolitan Industrial Technology Research Institute
-
Tanaka Shinichi
Tokyo Metropolitan Tama Small And Medium-sized Business Promotion Center
-
Hirose Norimitsu
Tokyo Metropolitan College Of Aeronautical Engineering
-
TANAKA Shin-ichi
Tokyo Metropolitan Tama Small and Medium-sized Business Promotion Center
-
Tanaka Shin-ichi
Tokyo Metropolitan Industrial Technology Research Institute
-
Tanaka Shin-ichi
Tokyo Metropolitan Industrial Technology Research Insitute
関連論文
- Nondestructive Evaluation of Sintered Iron Using Dynamic Young's Modulus Testing
- Effect of Brighteners on the Deposits in the Nickel Citrate Electroplating
- Influence of the Residual Aluminum in Raney-Nickel on the Catalytic Ability for Hydrogen Evolution Reaction (論文特集号 電解科学技術の進展)
- In Situ Observation of Sintered Iron and Carbon Steel Compacts Using a Low-Temperature Acoustic Microscope
- Poisson's Ratio of Sintered Materials for Structural Machine Parts (特集 自動車に関連する粉体および粉末冶金技術)
- Influence of Measuring Method on Young's Modulus and Comparison with Young's Modulus and Mechanical Property of Sintered Irons
- Investigation of Porosity Dependence for Elastic Modulus of Sintered Irons
- Ultrasonic Measurement of Lipid Bilayer Transition in The Presence of Melittin : Physical Acoustics
- Burst Cutting Area (BCA) Technology, A Recording Method for Disc Unique ID on ROM type DVD Disc