MAによるNi<SUB>33</SUB>Zr<SUB>67</SUB>混合粉末の非晶質化におよぼすミリング条件の影響
スポンサーリンク
概要
- 論文の詳細を見る
Effect of milling mode (the ratio of milling period to pause one) on amorphization of mixed Ni<SUB>33</SUB>Zr<SUB>67</SUB> powders by mechanical alloying(MA) was examined using high-speed vibratory ball mill. Three modes were determined by measuring temperatures on inner wall of vessel during MA with Chromel-Constantan(CRC) thermocouple, that is, mode A(the maximum temperature reached at 370 K), mode B(the maximum one 423 K) and continuity(continuous milling. 480 K after 150 ks of milling). The amorphization rate of the specimen by the mode A milling was slower than that by the continuous one, judging from the results of X-ray diffractometry and differential scanning calorimetry. Also, the thermal stability of the amorphous phase obtained was higher in this order: continuity, mode B and mode A.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 28a-ZP-1 メカニカルアロイング法により作成したNiHf非晶質合金の摂動角相関法による研究
- 1a-X-3 Ni-Hf非晶質合金の摂動角相関法による研究
- 28a-T-8 摂動角相関法による非晶質Ni-Nf合金の研究
- Al_Pd_M_混合粉末のメカニカルアロイング過程
- Ni77B23-xSix(x=3,5,6.5)およびNi77.5B14.6Si7.9非晶質合金の結晶化過程
- 4p-Q-12 Ni基非晶質合金の結晶化過程
- 2a-KE-11 鉄系アモルファス合金の構造緩和
- 12a-B-9 非晶質合金2605SC,2826Aの熱処理に伴う電気抵抗変化
- メカニカルアロイングによる非晶質Al_Cu_V_合金の作製とその構造変化
- MAによるNi33Zr67混合粉末の非晶質化におよぼすミリング条件の影響
- AgおよびDy混合粉末のメカニカルアロイング挙動
- メカニカルアロイングによるNiおよびZr混合粉末(Ni-rich組成領域)の非晶質化
- メカニカルアロイングによるNiおよびZr混合粉末の非晶質化
- 一方向凝固によるAl-Cu合金の組織 : モルフォロジー
- 25p-T-5 Fe-Si合金薄膜に成長する樹枝状組織
- Si-Au contactによるSiの成長 (IV) : 結晶成長
- 6a-M-11 微結晶面に生ずる局部融解
- 異種金属間の接触面に起る融解現象(I)(金属)
- メカニカルアロイングによるAl_Cu_Fe_混合粉末の準結晶化過程