フェロクロム粉の粉末冶金への応用について
スポンサーリンク
概要
- 論文の詳細を見る
Low carbon ferrochrome ingot contaning about 45% Cr was reduced to powder by means of σ phase brittleness brought about as a result of heat treatment at about 800°C.<BR>Whether the application for powder metallurgy of the ferrochrome powder was proper or not was examined.<BR>1) Powder ferrochrome crushed by means of σ phase brittleness is dense and square shaped with property to be easily made fine powder.<BR>2) Green strength of compact, while it is reduced in proportion to increase of ferrochrome powders content, shows a certain degree of intensity that makes possible of using them, even in case of containing 25% of chrome in the event of compact pressure at 5ton/cm<SUP>2</SUP>.<BR>3) In case of containing 13%, 18%, and 25% of chrome, compacts at 3 to 5ton/cm<SUP>2</SUP> of compacting pressure are sufficiently diffused by sintering at 1300°C for about 3 hours.<BR>4) Tensile strength of compacts in case of 3) shows 27-28kg/mm<SUP>2</SUP>, and 28-30kg/mm<SUP>2</SUP> where was heat treated.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- ステンレス鋼および耐熱鋼に対する希土類元素処理
- 154 耐熱合金への RE-Ca-Si 合金の添加 : ステンレス鋼に対する希土類元素処理 III(性質, 日本鉄鋼協会第 66 回(秋季)講演大会講演大要)
- 152 18Cr および Cr-Mn ステンレス鋼への R-Ca-Si 合金の添加 : ステンレス鋼に対する希土類元素処理 II(ステンレス鋼, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
- 114 含 N ステンレス鋼への N 添加合金について(ステンレス・分析, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 複合脱酸剤の応用とその製造について (I)
- フェロクロム粉の粉末冶金への応用について
- クロムボライドの精製について