銅フェライトの多形転移におよぼす機械的処理効果
スポンサーリンク
概要
- 論文の詳細を見る
Effect of mechanical treatment on the polymorphic transformation in copper ferrite was investigated by X-ray diffraction analysis. The results obtained are as follows: 1) The transformation from cubic to tetragonal structure at temperatures between 320°C and 360°C was promoted by the mechanical treatment such as pressing or milling. The transformation isotherms were represented by Danders equation, and the activation energy of the transformation was about 45k cal/mol, which was independent of the mechanical treatment and agreed with that of the oxidation. 2) For long-time milled or ground samples, the trans-formation from cubic to tetragonal structure did not occur below about 500°C. However, after being annealed higher temperatures the transformation occurred. 3) The tetragonal structure transformed into the cubic one at room temperature by long-time milling or grinding. It is considered that the cooperative Jahn-Teller ordering was destroyed by lattice imperfections, such as dislocations and stacking fault generated by milling or grinding. 4) The residual tetragonal structure which had not been transformed was transformed into the cubic one by heating above about 360°C.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 投射型カラーブラウン管用発光材料の進歩と課題
- 1)電子線照射による蛍光体の劣化の評価(テレビジョン電子装置研究会(第142回))
- 投射形ブラウン管用硫化カルシウム蛍光体
- Cuフェライトの相転移に及ぼす粉砕効果
- CuFe_2O_4の粉砕および加熱処理による正方晶-立方晶転移
- 銅フェライトの多形転移におよぼす機械的処理効果
- LiMnZnフェライトの焼結およびメモリコア特性に及ぼす粉砕効果
- LiMnZnフェライトの加熱処理による化学的性質の変化
- スピネル型フェライト粉体のメカノケミストリー