粉末圧延法による自己潤滑性焼結板の開発(第二報) : 圧延板と軟鋼との接合について
スポンサーリンク
概要
- 論文の詳細を見る
In order to evaluate the joining between steels and the powder rolling sheets, the bonding conditions considering the role of the porosity, were investigated as functions of sintering temperature, sintering time and bonding pressure under the condition of dissociated ammonia gas atmosphere. Results obtained were as follows:<BR>(1) As a constant sintering time, the tensile strength of the joints increased at elevated bonding pressure. However, no particular change was recognized for the hardness of crystalline in the matrix phase.<BR>(2) The growth of crystallines and the increasing of pores between graphite and matrix phase were restrained with increasing the bonding pressure.<BR>(3) During tensile test, the specimens were broken outside the joint area in cases of sintering temperatures of 1150 K, 1200 K and 1250 K at the bonding pressure of 0.15 MPa. The increase of temperature and time during the sintering reduced porosities in the contact area, and in addition, the extension of diffusion layers were observed by EPMA.
- 社団法人 粉体粉末冶金協会の論文
著者
-
菅藤 昭良
オイレス工業(株)
-
白坂 康広
オイレス工業(株)
-
松田 哲也
オイレス工業
-
山田 眞二
オイレス工業
-
跡部 敏郎
オイレス工業(株)
-
松田 哲也
オイレス工業(株)
-
山田 眞二
オイレス工業(株)
関連論文
- 境界潤滑下における高すずアルミニウム軸受合金の耐摩耗性
- Al-3-9%Sn-Si-Cu系鋳造合金の摩擦摩耗
- Al-Sn-Si-Cu 系鋳造合金の摩耗
- Al-Si-Cu系合金の摩耗に及ぼすYAGレーザー照射の影響
- 黒鉛分散した過共晶Al-23%Si-6%Cu-1%Mg合金複合材の摺動特性
- 黒鉛粗大化処理鋳鉄粉を用いた焼結材の摺動特性
- 境界潤滑下におけるアルミニウム合金の摺動特性
- 黒鉛分散 Al-Si-Cu 系合金の摺動特性
- 固体潤滑材分散青銅系焼結軸受の開発(第2報) : 青銅系圧粉体の焼結緻密化におよぼすV添加の影響
- 固体潤滑材分散青銅系焼結軸受の開発(第1報) : 青銅圧粉体へのCr添加による焼結緻密化促進について
- 境界潤滑下におけるAl-Si-Cu-Mg系合金の摺動特性に及ぼすけい素と銅添加量の影響
- 粉末圧延法による黒鉛含有銅合金摺動板の製造方法の開発
- 粉末圧延法による黒鉛含有焼結軸受の製造法
- 粉末圧延法による自己潤滑性焼結板の開発(第二報) : 圧延板と軟鋼との接合について
- 粉末圧延法による自己潤滑性焼結板の開発(第一報) : 黒鉛を含む銅―ニッケル―すず系の粉末圧延条件について
- オイルレス軸受