Mo<SUB>2</SUB>FeB<SUB>2</SUB>系硬質合金の焼結機構におよぼすCrおよびMo量の影響
スポンサーリンク
概要
- 論文の詳細を見る
The liquid phase sintering of Fe-6 wt%B-(38-53) wt%Mo-(0-10) wt%Cr alloys is studied by means of DTA, dilatometric measurements and microstructural observations. In addition, the mechanical properties of the sintered alloys are discussed. The results can be summarized as follows.<BR>(1) With the increase of the Cr content, the temperature ranges of L<SUB>1</SUB> and L<SUB>2</SUB> reactions, γ-Fe+Fe<SUB>2</SUB>B→L<SUB>1</SUB> and γ-Fe+Mo<SUB>2</SUB>FeB<SUB>2</SUB>→L<SUB>2</SUB>, shift to higher temperature.<BR>(2) As the Mo content increases, the temperature ranges of the L<SUB>1</SUB> and the L<SUB>2</SUB> reactions rise up when the Cr content is fixed.<BR>(3) The Cr distributes uniformly in Mo<SUB>2</SUB>FeB<SUB>2</SUB>, in the hard phases containing a small amount of Fe<SUB>2</SUB>B and in a ferrous binder.<BR>(4) Transverse-rupture strength values around 2.0 GPa are obtained for the Cr content up to 5 wt%.
著者
関連論文
- 急速凝固粉末を用いたジルコニア含有ムライトセラミックス焼結体の高温変形
- Cr_3C_2-Ni系サーメットと炭素鋼の焼結結合
- Crを含有したMo_2NiB_2系硬質合金の特性および組織に及ぼすW添加量の影響
- Cr_3C_2-Ni系サーメットの焼結性に及ぼすWB添加の影響
- Bi-Te化合物焼結体の熱電特性に及ぼす酸素量と結晶粒度の影響
- 546 硬質焼結合金の諸特性と焼結機構の考察(工具鋼, 材料, 日本鉄鋼協会第 108 回(秋季)講演大会)
- Mo_2NiB_2系硬質合金の焼結過程に及ぼすCrBの影響
- V添加Mo_2NiB_2系硬質合金の組織と機械的特性
- 鉄硼化物系硬質合金の焼結機構 (焼結--理論,プロセス技術)
- Mo2FeB2系硬質合金の焼結機構におよぼすCrおよびMo量の影響
- Mo2FeB2系硬質合金の焼結機構におよぼすNiおよびC量の影響
- Mo2FeB2系硬質合金の焼結機構におよぼす炭素量の影響 (超急冷合金・超硬質材料・イオン照射ナノメ-タコンポジット材料) -- (超硬質材料-1-)
- MO2FeB2系硬質合金の液相焼結機構におよぼすMo添加量の影響
- Mo2FeB2硼化物系硬質合金の焼結機構と機械的性質
- 鉄複ほう化物系サーメットのすべり摩耗特性(複合材料)
- 768 複硼化物系硬質合金の耐摩耗性(複合材料, 萌芽・境界技術, 日本鉄鋼協会第 109 回(春季)講演大会)
- 高耐食・高耐摩耗KHスクリュ, シリンダーの諸特性
- Mo2FeB2系硬質合金の焼結機構におよぼすCrおよびMo量の影響
- 鉄-モリブデン複硼化物系硬質合金の特性および組織におよぼすMo/B原子比の影響
- Mo2FeB2系硬質合金の焼結機構におよぼすNiおよびC量の影響
- Mo2FeB2系硬質合金の焼結機構におよぼす炭素量の影響
- Fe2B硼化物系硬質合金の焼結機構と機械的性質
- Mo2FeB2系硬質合金の液相焼結機構におよぼすMo添加量の影響
- Mo2FeB2硼化物系硬質合金の焼結機構と機械的性質
- 鉄硼化物系硬質合金の焼結機構