アトマイズ法によるAl-Pb合金粉末の凝固組織
スポンサーリンク
概要
- 論文の詳細を見る
By blowing nitrogen gas into the molten state of Al-5 to 50%Pb alloys, which was discharged from the molten metal nozzle at the bottom part of graphite crucible, powder was produced. The solidification structure and cooling rate of the powder were examined. The results obtained are summarized as follows: The particle shape was not spherical but tear-drop-like, and the particle size was from 10 to 500 μm. It was found that lead particles were dispersed in the aluminum matrix in all the cases. The cooling rate of this powder was from 50 to 5800 k/s. The value of the heat transfer coefficient at the powder-gas interface was from 89 to 577 J/m<SUP>2</SUP>.s.k.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- Bi添加LaMnO_3のXPS分析と磁性
- 1. 銅及び銅合金溶解の基礎
- ペロブスカイト型構造La_Sr_xMnO_3の磁気抵抗効果のSr組成比依存性
- ダイカスト研究部会レビュー
- La_Bi_XMnO_3系磁性と超巨大磁気抵抗効果
- La_Bi_xMnO_3Jahn-Teller 効果とXPS測定
- La_Bi_xMnO_3構造と電気的磁気的特性
- 紀要工学部記念号発刊に際して (新工学部記念号)
- 過共晶Al-Si合金の表面層に及ぼす振動の影響
- Mg-Li-Al鋳造合金の衝撃値に及ぼすAl量の影響
- Mg-Li鋳造合金の応力拡大係数
- 亜鉛合金ダイカストの現状
- 過共晶Al-Si合金の初晶けい素と湯じわに及ぼす振動の影響
- Mg-Li鋳造合金の旋削被削性に及ぼすAl添加の影響
- Zn-Al-Cu合金鋳物の偏析
- 過共晶Al-Si合金の初晶けい素に及ぼす超音波振動の影響
- Al-4.5mass%Cu合金鋳物の表面層組織に及ぼす振動の影響
- Ng-Li鋳造合金の健全性に及ぼすAl添加の影響
- 希土類-鉄-ボロン系磁石の組織と性質に及ぼす添加元素の影響
- Inconel 713LC合金の一方向凝固組織
- Inconel 713C 合金の凝固組織
- Mg-Li鋳造合金の旋削被削性
- MgおよびMg-Li合金のミクロ組織と性質に及ぼすCa添加の影響
- オ-ステンパ-ダクタイル鋳鉄の機械的性質と磁気的性質の相関関係
- Al-4.5% Cu 合金鋳塊の表面層における初晶の形態について
- Zn-Al合金の凝固組織
- 連続鋳造法による純銀および銀合金丸棒の製造
- Zn-Al-Cu合金の凝固組織に及ぼす冷却速度の影響
- Al-4.5%Cu合金鋳塊表面層におけるディスク組織構造の形成機構
- Al-4.5mass%Cu合金鋳物の表面偏析について
- Al-Cu合金鋳塊の表面層組織に及ぼす銅含有量の影響
- Al-4.5mass%Cu合金鋳塊のプリデンドライト組織と鋳型表面形状の関係
- 鋳物の表面層組織に及ぼす過熱度の影響
- プリデンドライトに及ぼす溶湯圧の影響
- 純金属の凝固組織と熱伝達
- 純金属の凝固時における鋳型壁への熱伝達
- Al-Cu合金のプリデンドライト形成の過冷度の関係
- アトマイズ法によるAl-Pb合金粉末の凝固組織
- アトマイズ粉末の凝固