Partition Coefficients of Alloying Elements to Primary Austenite and Eutectic Phases of Chromium Irons for Rolls.
スポンサーリンク
概要
- 論文の詳細を見る
The partition coefficients of chromium and carbon to primary austenite were measured on Fe-Cr-C ternary alloys containing 1.1 to 3.6 mass% C and 1.5 to 26 mass% Cr. Each alloy specimen was held for 1 h at a temperature just below the liquidus and then quenched in water cooled copper mold. Partition coefficients were in the range of 0.53 to 0.80 for chromium and 0.25 to 0.38 for carbon. Partition coefficients of third elements to primary austenite were also evaluated on 5 and 15 mass% Cr quaternary alloys. The coefficients of silicon, nickel and copper were larger than unity and increased with an increase in carbon content, while those of molybdenum, manganese and vanadium were smaller than unity and decreased with increasing carbon content of alloy. The partition coefficient of chromium was little influenced by the third elements.The partitions of alloying elements between liquid and eutectic phases were evaluated on eutectic alloy specimens with 2, 5, 15 and 30 mass% Cr that were quenched during freezing unidirectionally at 10 mm/h. The irons containing 2 and 5 mass% Cr froze in austenite+(Fe, Cr)3C eutectic, and the 15 and 30 mass% Cr irions crystallized into austenite+(Cr, Fe)7C3 eutectic. In each alloy system chromium, molybdenum, manganese and vanadium were distributed preferentially to eutectic carbide, white silicon and nickel dissolved selectively into eutectic austenite. The partition coefficient of each alloying element to eutectic, defined as the ratio of the average eutectic composition at cell tip to alloy content of liquid near freezing front, were also determined in this study.
- The Iron and Steel Institute of Japanの論文
著者
-
Ogi Keisaku
Department Of Materials Process Engineering Graduate School Of Engineering Kyushu University
-
Ono Yukinori
Department of Materials Science and Engineering, Faculty of Engineering, Kyushu University
-
Murai Noriko
Department of Materials Science and Engineering, Faculty of Engineering, Kyushu University
関連論文
- Thermal and Solutal Influences of Continuous Fibers on Matrix Dendrite Growth in Composite Materials
- Dendrite Growth of Aluminum-Copper Alloy Reinforced with Continuous Alumina Fibers
- Influence of Heat Treatment on the Distribution of Ni_2Nb and Microsegregation in Cast Inconel 718 Alloy
- Influence of Rhenium and Cooling Rate on the Solidification of Ni Base Superalloys, Inconel 718
- Solidification Process and Behavior of Alloying Elements in Ni-Based Superalloy Inconel718
- Glass-Metal Continuous Functionally Gradient Materials for Reflector Lamp
- Primary Dendrite Growth of Al-Cu Alloy Films between Solid Plates
- Analytical Study of the Growth and Formation Processes of Faceted 123 Crystals in Superconductive REBCO Oxide
- Influence of Solidification Microstructure and Distribution of Reinforcement on Fatigue Characteristics of Notched SiC Reinforced AC4B Alloy Composites
- Notch Size Effects in the Fatigue Characteristics of Al-Si-Cu-Mg Cast Alloy
- Influence of Nb and V on the Microstructure of Ni-Hard Type Cast Iron for Hot Steel Strip Mill
- Effect of Twin Growth on Unidirectional Solidification Control of Multicrystal Silicon for Solar Cells
- Partition Coefficients of Alloying Elements to Primary Austenite and Eutectic Phases of Chromium Irons for Rolls.
- Application of Discharge Implantation Method to Measurement of Diffusion Coefficient of Hydrogen Isotopes in Zirconium.