複合材料へのCVDの応用

スポンサーリンク

概要

• 論文の詳細を見る

• CVI (Chemical Vapor Infiltration) and pulse CVI process are reviewed. CVI is prominent in tight bonding between reinforcing fiber and matrix, however, is inferior in tedious processing time, nonuniformity of infiltration along the thickness and a limitation of the shapes of preform. On the contrary, powder-and fiber-preforms and porous materials with free shape can be infiltrated by pulse CVI. Pulse CVI of SiC from CH3SiCl3-H2 to porous carbon resulted in oxidation resistance over 1070h at 1573K in an air flow, and also increase of flexural strength by 2-3 times. RF-heated carbon fiber wound around carbon plate was effectively infiltrated by SiC. SiC powder preform, average particle size of 10μm, was strengthened to flexural strength of 240MPa after 30000 pulse of CVI. A combination of Si3N4 powder and BN matrix is also refered.

• 大同特殊鋼株式会社の論文

著者

• 杉山 幸三

  名古屋大学工学部

関連論文

• OMCVDによるZrO_2-MgO系薄膜の作製(イオン伝導性セラミックス)(導電性セラミックス)
• β-Li_xV_2O_5焼結体に関する物理化学的研究
• プラズマCVDで得られたAlN被覆黒鉛の耐酸化特性
• 複合材料へのCVDの応用
• ZrO_2-12mol%Y_2O_3単結晶の導電率の温度依存性

スポンサーリンク