Microstructure and ferroelectric properties of spark plasma sintered Li substituted K0.5Na0.5NbO3 ceramics
スポンサーリンク
概要
- 論文の詳細を見る
Potassium sodium niobate (KNN) is a well known piezoelectric material and a developing candidate for replacing lead based high performance piezoceramics due to limitations of hazardous materials in electronic devices. Lithium substitution in KNN structure leads a crystal transition from orthorhombic to tetragonal symmetry at room temperature and enhances ferroelectric properties. In this study, lithium substituted KNN piezoceramics with high relative densities were prepared by spark plasma sintering (SPS). Densification, crystal structure, microstructure and ferroelectric behavior of the samples were investigated. It was observed that lithium niobate based secondary phases exist in sintered KNN ceramics. These secondary phases showed significant effects on ferroelectric properties. Maximum (Pm) and remnant (Pr) polarizations were determined as 27 and 20 µC/cm2, respectively for pure KNN at the electric field of 20 kV/cm. When the electric field was increased to 30 kV/cm, Pm did not change significantly, but remained below Pr. For Li substituted samples, Pr decreased with increasing Li content.
著者
-
SEN Canhan
Istanbul Technical University, Metallurgical and Materials Engineering Department
-
ALKAN Berk
Istanbul Technical University, Metallurgical and Materials Engineering Department
-
AKIN Ipek
Istanbul Technical University, Metallurgical and Materials Engineering Department
-
YUCEL Onuralp
Istanbul Technical University, Metallurgical and Materials Engineering Department
-
SAHIN Filiz
Istanbul Technical University, Metallurgical and Materials Engineering Department
-
GOLLER Gultekin
Istanbul Technical University, Metallurgical and Materials Engineering Department
-
Akin Ipek
Istanbul Technical Univ. Dep. Of Metallurgical And Materials Engineering
-
Goller Gultekin
Istanbul Technical Univ. Dep. Of Metallurgical And Materials Engineering