Influence of laboratory light sources on the wear characteristics of indirect composites
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of the current study was to evaluate the influence of light sources on the mechanical properties and wear characteristics of indirect composite materials. The two composite materials used were Estenia C&B and Epricord. The three laboratory polymerization units used, of which the wavelength range was 400–500 nm, were Hyper LII (two metal halide lamps of 4.82 mW/cm2), α-Light II (one halogen lamp and two fluorescent tubes of 3.60 mW/cm2), and Labolight LV-II (three fluorescent tubes of 0.63 mW/cm2). Three-body wear test was performed using indirect composite plate specimens, a gold alloy antagonist, and a polymer slurry. Wear depths of Estenia C&B polymerized with Hyper LII, α-Light II, and Labolight LV-II were 5.7, 18.5, and 64.2 μm respectively, whereas those of Epricord were 12.9, 18.7, and 48.5 μm respectively. Results showed that, after 100,000 cycles of localized loading, high-intensity light sources were effective in enhancing the wear resistance of both composite materials.
論文 | ランダム
- HANSEN, MOGEN HERMAN, The Athenian Assembly in the Age of Demosthenes, pp. viii+249, Blackwell, Oxford/New York 1987 / HANSEN, MOGEN HERMAN, The Athenian Ecclesia, 2 vols., pp. x+245, viii+324, Museum Tusculanum Press, Copenhagen, 1983/89.
- i) FINLEY, M. I., Economy and Society in Ancient Greece., Pp. xxvi+326, Chatto & Windus, London, 1981. / ii) FINLEY, M. I., Ancient Slavery and Modern Ideology., Pp. 202, Chatto & Windus, London, 1980.
- 紀元前5,4世紀のアテナイにおける海上貿易とεκδοσι&b.sigmav;
- 広島市まんが図書館あさ閲覧室オープン--公立初の漫画専門図書館の運営から (特集 図書館でマンガを提供するには)
- 広島市まんが図書館繁盛記--開館して2年がたちました