SBRを添加したコンクリートの耐久性に関する実験的検討
スポンサーリンク
概要
- 論文の詳細を見る
It has been known that durability of mortar is improved by addition of polymer. We assume that the addition of polymer is one of technologies about extension of life-span of concrete. Experimental studies about mechanical property, durability and property of drying shrinkage cracking of concrete added SBR were carried out. As a result, strength of concrete added SBR was the same degree or greater than normal concrete. Carbonation depth was decreased as the ratio of SBR were increased. Relative dynamic modulus of elasticity of the concrete added SBR under on resistance of freezing and thawing test was much the same of normal concrete added an air entraining agent. No cracks had occurred for 55days on drying shrinkage cracking test when SBR were added to 10% weight ratio of cement.
著者
-
熊野 知司
摂南大学都市環境システム工学科
-
高見 新一
大阪産業大学工学部土木工学科
-
熊野 知司
摂南大学 工学部都市環境システム工学科
-
中川 佳祐
摂南大学大学院工学研究科社会開発専攻
-
井上 善彦
前田工繊（株）環境資材事業本部
-
高見 新一
大阪産業大学 工学部都市創造工学科
関連論文
- ポンプ圧送によるフレッシュコンクリートの性状変化に関する実験的検討
- 各種試験環境下におけるモルタルのASR膨脹特性
- ポリカルボン酸系高性能AE減水剤を用いた高流動ペーストの粘度の経時変化予測手法の検討
- ポリカルボン酸系高性能AE減水剤を用いた高流動ペーストの粘度の経時変化予測手法の検討
- ポリカルボン酸系高性能AE減水剤を用いたセメントペーストの粘度の経時変化予測に関する考察
- ポリカルボン酸系高性能AE減水剤を用いたセメントペーストの粘度の経時変化予測手法に関する検討
- 高流動モルタルの流動性の経時変化予測に関する一考察(建設材料)
- 普通骨材を混合使用した再生骨材コンクリートのフレッシュおよび硬化性状に関する基礎的研究(建設材料)
- 再生骨材を混合使用したRC部材の力学的特性に関する研究
- 低品位フライアッシュのASR抑制に関する研究
- SBRを添加したコンクリートの耐久性に関する実験的検討
- 近畿地方の骨材需給の現況と近畿産骨材を使用したモルタルの乾燥収縮 : 近畿支部「性能評価型コンクリートに向けた骨材調査研究委員会」の報告
- ポンプ圧送に伴うフレッシュコンクリートの品質変化
- 1003 低品位フライアッシュのASR抑制に関する研究(骨材)
- 1010 各種試験環境下におけるモルタルのASR膨張特性(骨材)