低合金鋼のスモールパンチクリープ特性におよぼす試験片表面状況と雰囲気の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effects of various factors such as the surface finish condition of specimens, lubricant and argon gas flow rate on both the creep deformation behavior and time to rupture for 2.25Cr-1Mo low alloy steel used for boilers by small punch testing were studied. There was little difference in both the small punch creep deformation behavior and time to rupture due to the difference in surface roughness between #1200 polished specimens and those in mirror polished condition. The application of BN lubricant to the specimen surface resulted in the decrease in time to rupture, due to the lowering of friction coefficient. Furthermore, the time to rupture increased according to the increase of argon gas flow rate. The depth analysis by μ-ESCA for surface oxide film formed in an argon gas atmosphere demonstrated that the formation of Fe-rich oxide film with a low friction coefficient produced a decrease in time to rupture under a low argon gas flow rate condition. The formation of Cr-rich oxide film with high friction coefficient produced the increase in time to rupture under high argon gas flow rate condition. This suggests that the reliable control of argon gas flow rate is very important in order to evaluate the life of material by small punch creep testing.
著者
-
西岡 智也
住友金属テクノロジー(株)
-
植村 啓美
関西電力(株)電力技術研究所
-
大澤 敏幸
住友金属テクノロジー(株)
-
椹木 義淳
住友金属テクノロジー(株)
-
椹木 義淳
住友金属テクノロジー(株)受託研究事業部
-
椹木 義淳
住友金属テクノロジー(株)
-
大澤 敏幸
住友金属テクノロジー(株)
関連論文
- タービンロータ材のクリープ損傷に及ぼす二軸応力の影響
- 低合金鋼のスモールパンチクリープ特性におよぼす試験片表面状況と雰囲気の影響
- USCボイラ用高強度高耐食23Cr-43Ni-6W鋼の高温強度と組織
- マルテンサイト系耐熱鋼のクリープ変形に及ぼす予時効の影響
- マルテンサイト系耐熱鋼のクリープ変形に及ぼすWの影響
- OS6-11 実機高中圧タービンロータの脆化度調査(OS6 設備診断・運用保全技術,分散と集中の共存)
- 2.超々臨界圧エネルギー機器と極長時間高温強度(「超」あるいは「極」の技術と高温強度)
- TypeIV Damage Evaluation of Low Alloy Steel Weld Joint by Small Punch Creep Testing