Using Electrical Resistance Change to Monitor the Damage in a Thick CFRP Plate Caused by a Dent
スポンサーリンク
概要
- 論文の詳細を見る
An impact load on a thick carbon fiber reinforced plastic (CFRP) plate usually causes a dent. The dent results in a decrease of electrical resistance. Our previous paper demonstrated the effect of the dent in the measurement of electrical resistance change of a thick CFRP plate subjected to impact loading. The present paper focuses on the electrical resistance decrease caused by the dent. Numerous FEM analyses were performed, and the relationship between electrical resistance changes and delamination location was constructed, by measuring the response surfaces. Several experiments were conducted and the measured electrical resistance changes were used to predict damage location from the response surfaces. The present study shows that the dent decreases the electrical resistance change ratio even in the adjacent segments, and the electrical resistance changes caused by the dent enable us to monitor the damage location. FEM analyses for a projected area model are sufficient to construct the relationships without resorting to many experiments.
著者
-
TODOROKI Akira
Department of Mechanical Science and Engineering, Tokyo Institute of Technology
-
MATSUZAKI Ryosuke
Department of Mechanical Science and Engineering, Tokyo Institute of Technology
-
SHIMAZU Yasuhiro
Tokyo Institute of Technology
-
MIZUTANI Yosihiro
Department of Mechanical Sciences and Engineering Tokyo Institute of Technology
関連論文
- Transient and Dynamic Stress Analysis of Functionally Graded Thick Hollow Cylinder Subjected to Thermal Shock Loading Using an Analytical Method
- Fiber-waviness Model in Filament Winding Process
- New Surrogate Model to Predict Fracture of Laminated CFRP for Structural Optimization
- Using Electrical Resistance Change to Monitor the Damage in a Thick CFRP Plate Caused by a Dent
- Unsupervised Structural Damage Diagnosis Based on Change of Response Surface Using Statistical Tool : Application to Damage Detection of Composite Structure
- 114 Bearing Failure Detection of Bolted Composite Joints Using Electric Resistance Change Method
- Structural Health Monitoring : Sensors, Diagnostic Method and System
- Application of Electric Potential Method to Smart Composite Structures for Detecting Delamination
- Electrical Resistance Change of CFRP under a Compression Load
- Electrical Resistance Change of Thick CFRP Laminate for Self-Sensing
- Durability Estimates of Copper Plated Electrodes for Self-sensing CFRP Composites
- Mechanism of Electrical Resistance Change of a Thin CFRP Beam after Delamination Cracking
- Stacking-Sequence Optimization of Composite Delta Wing to Improve Flutter Limit Using Fractal Branch and Bound Method
- Electrical Resistance Reduction of Laminated Carbon Fiber Reinforced Polymer by Dent Made by Indentation without Cracking