Ni-Cr-Mo-B系ガスアトマイズ粉末の複硼化物生成挙動に及ぼすB量および熱処理の影響
スポンサーリンク
概要
- 論文の詳細を見る
Effects of B content and heat treatment on properties of gas atomized powders with Ni-10mass%Cr-36mass%Mo-Xmass%B compositions (X=1.5∼4) were investigated. Examined powders were produced by gas atomization, followed by sieving under 150 μm. These powders were heat treated at various temperatures to investigate the effect of heat treatment temperature.As a result, tetragonal M3B2, tetragonal M5B3 and orthorhombic M3B2 type complex borides were observed in examined powders before and after the heat treatment. Compositions and crystal structures of complex borides varied depending on B contents in examined powders, hereby compositions of Ni-based matrix phases also varied. Vickers hardness after the heat treatment at 1473 K increased with increasing B content.
著者
関連論文
- 耐熱亀裂性に優れた連鋳ロール肉盛用Ni基超合金の開発
- ショットピーニング投射材用1200HV級FeCrBガスアトマイズ粉末の開発
- ガスアトマイズ法で作製したショットピーニング用Fe-Cr-B合金投射材の寿命特性
- 粉末多孔体流路型燃料電池セパレータの開発
- パルス圧力付加オリフィス噴射法による単分散Fe系金属ガラス合金粒子の作製と評価
- 精密ホットプレスを用いたNi基金属ガラス粉末の焼結特性
- Ni基金属ガラス粉末の温間塑性加工・焼結特性
- SCM420ガス浸炭材の表面残留応力および疲労特性に及ぼすHV1200級Fe-Cr-B投射材を用いた二段ショットピーニングの影響
- 超耐食・耐摩耗性を有する硼化物分散Ni基合金の開発
- 二次加工による機能性ガスアトマイズ合金粉末の特性向上研究
- インバー系ガスアトマイズ粉末不定形状化に及ぼす添加元素とガス種の影響
- 電磁波吸収特性に及ぼす粉末の粒度および塑性加工の影響
- SUS316L粉末RIP成形焼結体の密度に及ぼす粉末条件の影響
- ショットピーニング投射材用1200HV級FeCrBガスアトマイズ粉末の開発
- 643 粉末熱間押出し法によるセンダストの特性(粉末・急冷金属, 萌芽・境界技術, 日本鉄鋼協会第 113 回(春季)講演大会)
- ショットピーニング用Fe-Cr-B系ガスアトマイズ粉末の諸特性に及ぼすB量の影響
- ショットピーニング用1200HV級Fe-Cr-B系ガスアトマイズ合金粉末の開発
- Ni-Cr-Mo-B系ガスアトマイズ粉末の複硼化物生成挙動に及ぼすB量および熱処理の影響
- 冷間工具鋼の諸特性に及ぼすHV1200級Fe-Cr-B投射材を用いたショットピーニングの影響
- Ni-Cr-Mo-B系ガスアトマイズ粉末の複硼化物生成挙動に及ぼすB量および熱処理の影響
- Ni-Cr-Mo-B系ガスアトマイズ粉末の複硼化物生成挙動に及ぼすCr,Mo量および熱処理の影響 (特集 硬質材料の進展と課題(2))
- Fe-Cr-B系硬質ガスアトマイズ粉末の諸特性に及ぼす添加元素の影響
- Ni-Cr-Mo-B系ガスアトマイズ粉末の複硼化物生成挙動に及ぼすCr,Mo量および熱処理の影響
- HIP法で固化成形したNi-Cr-Mo-B系耐食耐摩耗合金の諸特性に及ぼすCr, Mo量の影響
- Fe-Cr-B系硬質ガスアトマイズ粉末の諸特性に及ぼす粒径の影響