LaSrAlFeO3−δ oxygen ion conducting membranes sintered under different atmosphere and HIP
スポンサーリンク
概要
- 論文の詳細を見る
La0.6Sr0.4AlxFe1−xO3−δ (LSAF) mixed ionic electronic conducting membranes have been sintered, and the substitution of Al for Fe reduced the density of the sintered body including large defect of pore channels. The sintering behavior of the La0.6Sr0.4Al0.1Fe0.9O3−δ samples have been studied under different oxygen partial pressure, PO_2, and a post process of hot isostatic pressing (HIP) has been carried out. The thermal expansion coefficients and the differential expansion ratios measured in air and under reducing atmosphere for these samples were 15.6 × 10−6/K−1 and 0.37%, respectively, and were not affected by the sintering process. The density of the sample sintered in air was 96.5% and the HIP increase the density of the sample up to 99.6%, eliminating the pores. The three point flexural strength of the HIP sample at 25 and 1000°C were 265 and 208 MPa, respectively, and the oxygen permeation rate of the HIP treated membranes with the thickness of 0.5 mm was 8 cc/min/cm2.
- 公益社団法人 日本セラミックス協会の論文
著者
-
TAKAHASHI Yosuke
Department of Cardiovascular Surgery, Fukui Cardiovascular Center
-
SHIN Woosuck
Department of Materials Science and Engineeing, KAIST
-
Shin Woosuck
Department Of Materials Science And Engineeing Kaist
-
Takahashi Yosuke
Department Of Cardiovascular Surgery Fukui Cardiovascular Center
-
SHIN Woosuck
Department of Frontier Materials, Nagoya Institute of Technology
-
TAKAHASHI Yosuke
Department of Frontier Materials, Nagoya Institute of Technology
関連論文
- Expanded polytetrafluoroethylene-valved conduit with bulging sinuses for right ventricular outflow tract reconstruction in adults
- Effects of Texturing and Microbridge length on the IR Responsivity of YBa_2Cu_3O_x Thin Film
- An Approach to Mitral Valve Surgery by a T-shaped Mini-sternotomy with Functioning Bilateral Internal Thoracic Artery Grafts
- Rupture of Aneurysmal Circumflex Coronary Artery Into the Left Atrium After Ligation of Its Arteriovenous Fistula
- LaSrAlFeO3−δ oxygen ion conducting membranes sintered under different atmosphere and HIP
- Effects of Pulling Direction on Directional Growth of YBa_2Cu_3O_ Superconductors
- Directional Growth of Extruded YBa_2Cu_3O_ Superconductors
- Long-term survival and functional recovery after isolated coronary artery bypass grafting in patients with severe left ventricular dysfunction
- Homemade Endovascular Treatment of Postoperative Aortobronchial Fistulas
- Successful Surgical Treatment of a Mycotic Right Coronary Artery Aneurysm Complicated by a Fistula to the Right Atrium