Direct Reduction Behaviors of Composite Binder Magnetite Pellets in Coal-based Grate-rotary Kiln Process

スポンサーリンク

概要

• 論文の詳細を見る

• Directly reduced iron is an imperative burden for EAF (electric arc furnace) to make good quality and special steel. As an alternative of direct reduction processes, an innovative coal-based direct reduction of composite binder magnetite pellets in grate-rotary kiln has been developed at Central South University and put into operation. A study of the direct reduction behaviors of composite binder magnetite pellets was carried out in a simulating coal-based grate-rotary kiln process in this paper. Preheated pellets made of magnetite concentrate and composite binder and fired oxide pellets containing bentonite as binder were directly reduced using non-coking coal as reductant in a tube furnace, and their reduction behaviors have been demonstrated by measuring reducibility, variations of compress strength, porosity, phases changes and micro structure under XRD, SEM and optical microscopy. It is shown that preheated pellets possess much better reducibility than fired oxide pellets. Superior reducibility of preheated pellets should be ascribed to their higher effective diffusivity due to higher porosity. The compressive strength of preheated pellets climbs quickly after reducing for 30 min and achieve a high value at the end of reduction, leading to smooth and intact metallized pellets whereas the compressive strength of metalized pellets from reducing of fired pellets is much lower, more cracks and fractures being formed. The preheated pellets possess self-curing function because of the multiple functions of composite binder, eliminate cracks and fractures and keep pellets intact during reducing, depressing reduction degradation and preventing accretion in rotary kiln.

著者

• Zhu Deqing

  School of Minerals Processing and Bioengineering, Central South University

• Mendes Vinicius

  School of Minerals Processing and Bioengineering, Central South University

• Chun Tiejun

  School of Minerals Processing and Bioengineering, Central South University

• Pan Jian

  School of Minerals Processing and Bioengineering, Central South University

• Li Qihou

  School of Minerals Processing and Bioengineering, Central South University

• Li Jian

  Research Institute of Baosteel

• Qiu Guanzhou

  School of Minerals Processing and Bioengineering, Central South University

関連論文

• Direct Reduction Behaviors of Composite Binder Magnetite Pellets in Coal-based Grate-rotary Kiln Process
• Constituents of Roots of Salvia deserta SCHANG. (Xinjiang-Danshen)
• Improving the Oxidizing Kinetics of Pelletization of Magnetite Concentrate by High Press Roll Grinding
• Characterization of Preparing Cold Bonded Pellets for Direct Reduction Using an Organic Binder
• Mechano-chemical Activation of Magnetite Concentrate for Improving Its Pelletability by High Pressure Roll Grinding
• Direct Reduction Behaviors of Composite Binder Magnetite Pellets in Coal-based Grate-rotary Kiln Process
• A Comparative Study of Alkaloidal Constituents in Corydalis decumbens Tubers by High Performance Liquid Chromatography
• Solid-State Dye-Sensitized Solar Cells Using Poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylene-vinylene] as a Hole-Transporting Material

スポンサーリンク