Deformed Microstructure of AZ91 Magnesium Alloy Impacted by Projectiles with Velocities of 2—3 km/s
スポンサーリンク
概要
- 論文の詳細を見る
AZ91 magnesium alloy in different heat treatment conditions was impacted by GCr15 steel projectile (2 km/s, power gun) and 2017 Al alloy projectile (3 km/s, two-stage light gas gun). Deformed bands, plastic flow and a wealth of cracks were observed near the crater in as-cast magnesium alloy impacted by GCr15 steel projectile, while for the solution treated alloy, both deformed and transformed bands were observed accompanied by fewer cracks near the crater. Upon higher velocity impact using two-stage light gas gun, many cracks and severe deformed areas containing a number of elongated grains were observed near the crater for both hot-forged and solution-treated targets, while fewer adiabatic shear bands could be found. Most of these shear bands were located at the end of cracks. The strain hardening at different zones under the crater was also investigated.
著者
-
Xu Cheng-yan
School Of Materials Science And Engineering Harbin Institute Of Technology
-
Zhen Liang
School Of Materials Science And Engineering Harbin Institute Of Technology
-
Shao Wen-zhu
School Of Materials Science And Engineering Harbin Institute Of Technology
-
XU Cheng-Yan
School of Materials Science and Engineering, Harbin Institute of Technology
-
JI Jian-Yu
School of Materials Science and Engineering, Harbin Institute of Technology
-
LI Guo-Ai
School of Materials Science and Engineering, Harbin Institute of Technology
-
ZOU Dong-Li
School of Materials Science and Engineering, Harbin Institute of Technology
関連論文
- Deformed Microstructure of AZ91 Magnesium Alloy Impacted by Projectiles with Velocities of 2—3 km/s
- Template-free Hydrothermal Preparation of Mesoporous TiO_2 Microspheres on a Large Scale
- Large-scale Synthesis of SrCrO_4 Nanowires and PbCrO_4 Nanorods by a Solution-phase Method at Room Temperature