Coating Degradation in Hot Press Forming
スポンサーリンク
概要
- 論文の詳細を見る
The thermo-mechanically induced microstructure changes occurring in a type 1 aluminized coating on hot press forming (HPF) steel were studied in detail. The formation of intermetallic phases at the soaking temperature prior to die quenching revealed that the coating matrix consists mainly of FeAl2 intermetallic phase by the time the press forming carried out. Kirkendall void formation was observed to take place. The thermal oxidation of aluminized coating during HPF was found to be limited, with the coating acting as an effective barrier for the oxygen during heating. The deterioration caused by the high temperature plastic deformation was shown to lead to coating cracking without loss of adhesion. The steel surface was oxidized where it was exposed between the coating segments.
論文 | ランダム
- クリティカルパスに対する患者の反応と看護師の認識調査
- 482 小児パイエル氏板T細胞の牛乳蛋白に対する免疫応答に関する検討 : Th1/Th2バランスについて
- 470 小児パイエル氏板T細胞の表面マーカーの解析 : 特に末梢血リンパ球との比較について
- PP-1545 ヒト肺癌細胞株を用いた同所性移植縦隔リンパ節転移モデルとその有用性
- F-18 CDDP及びUFTによるヒト肺癌細胞株の縦隔転移への影響 : SCIDマウスのリンパ行性転移モデルにおいて(MMP・間質・転移,第40回日本肺癌学会総会号)