Ni合金Alloy 718のき裂発生と伝ぱに及ぼす時効の影響
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate the effect of aging condition on initiation and propagation properties of a fatigue crack, rotating bending fatigue tests were carried out using partially notched specimens of Ni-base supper alloy, Alloy 718, at 500℃. Aging conditions selected were the under-aged and the over-aged conditions with nearly the same hardness. Fatigue strength of the over-aged alloy was higher than that of the under-aged one in wide life region till 108 cycles. Moreover, fatigue strength at 500℃ was larger than that at room temperature in both alloys. Most of fatigue life was occupied by the growth life of a small crack in both alloys. The main reason for higher fatigue strength of the over-aged alloy was an increase in crack growth resistance. Many slip bands were observed on the specimen surface of the over-aged alloy in comparison with results of the under-aged one. This related to the difference in crack growth resistances in both alloys.
著者
-
皮籠石 紀雄
鹿児島大学工学部
-
中村 祐三
鹿児島大学大学院理工学研究科
-
皮籠石 紀雄
鹿児島大学大学院理工学研究科
-
中村 祐三
鹿児島大学
-
仮屋 孝二
第一工業大学
-
川籠石 紀雄
鹿児島大学
-
吉見 祥吾
富士重工業(株)
-
森野 数博
徳山高専機械電気工学科
-
仮屋 孝二
第一工業大学機械システム工学科
関連論文
- 時効硬化Al合金押出し材の超音波疲労におけるせん断形き裂の伝ぱ
- 時効硬化Al合金の超音波疲労強度に及ぼす大気湿度の影響
- 超微細粒銅の疲労損傷と微小き裂進展挙動に及ぼす160℃焼なましの影響
- マルテンサイト系ステンレス鋼SUS420J2の疲労強度に及ぼす表面処理の影響
- Alloy 718の中高温下におけるき裂伝ぱ抵抗に及ぼす結晶粒径の影響
- 1252 インコネル718の中高温疲労におけるき裂伝ぱ抵抗(G03-9 材料力学(9)疲労・強度2,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- Ni基超合金インコネル718の超音波疲労特性に及ぼす結晶粒径の影響
- 617 インコネル718の超音波疲労(微視組織・き裂進展,疲労破壊の防止と評価,オーガナイスドセッション1)
- 601 マルエージング鋼の中高温下における疲労強度(環境,疲労破壊の防止と評価,オーガナイスドセッション1)
- 117 インコネル718の超音波疲労特性に及ぼす微視組織の影響(OS 材料利用・改質に関する実験・数値解析(その3))