Evaluation of Interfacial Tensile Strength in Glass Fiber/Epoxy Resin Interface using the Cruciform Specimen Method
スポンサーリンク
概要
- 論文の詳細を見る
Glass/epoxy interfacial tensile strength is investigated by the cruciform specimen method. The conventional transverse tensile test for single fiber composite is one of methods for evaluating the interfacial tensile strength, but stress singularity at the specimen edge is a very complicated problem to be solved. A cruciform specimen which has large width only around fiber embedded in transverse direction can potentially prevent the stress singularity problem. The cruciform specimen geometry is first discussed by means of finite element analysis considering experimental conditions. Transverse tensile test is conducted and an interfacial debonding which initiates at the middle of specimen not at edge is observed using the cruciform specimens. The interfacial tensile strength can be obtained by the value of stress concentration factor at interface multiplied by specimen stress. The location which the debonding initiates from is discussed and the validity of the evaluation method in this study is verified when interfacial tensile strength is as high as or lower than interfacial shear strength.
- 一般社団法人 日本機械学会の論文
著者
-
Ogihara Shinji
Department Of Mechanical Engineering Science University Of Tokyo
-
KOYANAGI Jun
Institute of Space and Astronautical Science, Japan Aerospace Exploration Agency
-
SAKAMOTO Yoriaki
Department of Mechanical Engineering, Tokyo University of Science
関連論文
- Strength Improvement on an Imaginary SiC Fiber of Ideal Diameter and Reduced Internal Defects Estimated from the Weibull Scaling of Tyranno ZMI Fiber(Recent Advances in Materials and Processing [II])
- Damage mechanics analysis for predicting mechanical behavior of general composite laminates containing transverse cracks
- Experimental characterization of the effects of stacking sequence on the transverse crack behavior in quasi-isotropic interleaved CFRP laminates
- Transverse cracking in CFRP cross-ply laminates with interlaminar resin layers
- Experimental characterization of microscopic damage progress in quasi-isotropic CFRP laminates : effect of interlaminar-toughened layers
- Analysis of stress and displacement fields in interlaminar-toughened composite laminates with transverse cracks
- Microscopic fatigue failure process in interleaved and toughness-improved CFRP cross-ply laminates
- Characterization of nonlinear behavior of carbon/epoxy unidirectional and angle-ply laminates
- 229 Experimental evaluation of fragmentation behavior in single carbon fiber composite
- 217 Nonlinear stress-strain behavior in CFRP laminates
- Mechanical and Thermal Properties of Short Coir Fibre Reinforced Poly(Butylene Succinate) Biodegradable Composites
- Mechanical Properties in a Bamboo Fiber/PBS Biodegradable Composite
- Development of High-Performance CFRP Flywheel
- Mixed-Mode Interfacial Debonding Simulation in Single-Fiber Composite under a Transverse Load
- Evaluation of Interfacial Tensile Strength in Glass Fiber/Epoxy Resin Interface using the Cruciform Specimen Method