Hydration Behavior of Blast Furnace Slag Activated by Na2SO4 and Fineness of Slag (第2回日韓資源リサイクル・材料科学に関する国際シンポジウム特集号)

概要

論文の詳細を見る
The effect of alkali activator and fineness of slag on the physical properties of blast furnace slag cement was investigated. Na2SO4 was used as an alkali activator in this study. Blast furnace slag cement was prepared from mixture of blast furnace slag, ordinary Portland cement, and anhydride gypsum. The fluidity and the compressive strength according to each mixture ratio of them were analyzed by using statistical analysis in order to discover the parameters influencing the fluidity and compressive strength. The results showed that the hydration of blast furnace slag took place by addition of Na2SO4, and ettringite with column-crystalline was created as main hydration product of blast furnace slag. And it is found that the compressive strength of blast furnace slag cement tends to increase as ordinary Portland cement content is higher until 3 days. However, it is also known that the compressive strength tends to increase with the increase of higher blast furnace slag content, along with increase in the OPC on 28 days. As a result of this analysis, it is considered that the ordinary Portland cement content influences the initial compressive strength of blast furnace slag cement, and that in later days is greatly influenced by slag content.
環境資源工学会の論文