Damage Behavior and Life Prediction in CFRP Cross-Ply Laminates under Fatigue Loading
スポンサーリンク
概要
- 論文の詳細を見る
This paper deals with fatigue damage and life prediction of CFRP cross-ply laminates. Fatigue tests are carried out on CFRP unidirectional and cross-ply laminates under the on-axis and off-axis directions. On the unidirectional laminate, fiber breakage and fiber-peeling develop before the final fracture under on-axis fatigue, while the final fracture suddenly occurs by cracking along the fiber direction under off-axis fatigue. On the cross-ply laminates, ply-cracking in 90° plies and fiber-peeling in 0° plies develop under on-axis fatigue, while ply-cracking and delamination lead to the final fracture under off-axis fatigue. Based on the comparison of damage behavior and S-N curves between unidirectional and cross-ply laminates, possibility of fatigue life prediction of CFRP cross-ply laminates is discussed.
著者
-
Tohgo Keiichiro
Department Of Iron And Steel Engineering Nagoya University
-
NAKAGAWA Shuji
Department of Mechanical Engineering, Shizuoka University
-
ARAKI Hiroyasu
Department of Mechanical Engineering, Shizuoka University
関連論文
- Characterization of Fracture Process in Ceramic-Metal Functionally Graded Material under Three-Point-Bending(Macro-, Micro-, Meso-, and Nano-scopic Strength of Materials Relating to Microstructures)
- Quantitative Dependence of the Effective Modulus of Particle Reinforced Composites on Partially Debonding Damage
- Finite Element Analysis of a Cracked Ellipsoidal Inhomogeneity in an Infinite Body and Its Load Carrying Capacity
- The Behavior of Ductile Crack Initiation from a Notch and a Crack Under Mode I Loading
- Ply-Cracking Damage and Nonlinear Deformation of CFRP Cross-Ply Laminate(Special Issue on strength and Fracture, and Experimental Mechanics)
- Ply-Cracking Damage and Nonlinear Deformation of CFRP Cross-Ply Laminate(Composite 2)
- Theory of Reinforcement Damage in Discontinuously-Reinforced Composites and Its Application
- Damage Behavior and Life Prediction in CFRP Cross-Ply Laminates under Fatigue Loading
- Ply-Cracking Damage Theory for Cross-Ply Laminate and Its Application to Finite Element Method
- The Influence of Debonding Damage on a Crack-Tip Field in Glass-Particle-Reinforced Nylon 66 Composite
- Applicability of Fracture Mechanics in Strength Evaluation of Functionally Graded Materials
- Incremental Theory of Particulate-Reinforced Composites Including Debonding Damage
- Fracture Mechanics Study on Stress Corrosion Cracking Behavior under Corrosive Environment
- Monte Carlo Simulation of Stress Corrosion Cracking on Smooth Surface of a Sensitized Stainless Steel Type 304 under Non-Uniform Stress Condition
- Characterization of Fatigue Strength and Damage Behavior in Glass-Particle-Reinforced Nylon 66 Composites