Repair potential of a laboratory-processed nano-hybrid resin composite

スポンサーリンク

概要

• 論文の詳細を見る

• The purpose of this study was to compare the 24-h composite-to-composite microtensile bond strength of Gradia Forte (GF) repaired with the same or a different material after different surface treatments. Different groups were set up, in which composite blocks of GF were subjected to the following treatments: Group 1, sandblasting with 50-μm aluminum oxide and 37% phosphoric acid etching (PA); Group 2, bur roughening and etching with 37% PA; Group 3, etching with 37% PA only. In all groups, a bonding resin was used as an intermediate agent prior to layering of the repair material (Gradia Direct (GD), Gradia (G), or GF). Bond strengths were then determined and analysed statistically. Scanning electron microscopy (SEM) evaluation of substrates and bonded interfaces was also performed. Surface treatment (P < 0.001) and repair materials (P < 0.001) were factors that significantly affected repair strength, whereas their interaction (P = 0.31) had no significant effect. Group 3 showed significantly superior repair strength to Groups 1 and 2, whereas Group 2 showed significantly weaker repair strength to Groups 1 and 3. Irrespective of surface treatment, GD and G gave similar results, which were better than those obtained using GF. The lowest probability of failure was found for GD and G in Group 3, whereas the highest was found for GF in Groups 1 and 2. Premature failures occurred mainly with G and GF. No pre-testing failures were found in the sandblasting/GD subgroup. Surface-treated composites showed different textures under SEM, whereas composite-repair bonds showed comparable interfacial features. (J. Oral Sci. 50, 403-412, 2008)

著者

• Ferrari Marco

  Department Of Biomedical Sciences And Technologies University Of L'aquila

• Polimeni Antonella

  Department of Dental Sciences, University of Rome "La Sapienza"

• Papacchini Federica

  Department of Dental Materials and Restorative Dentistry, University of Siena

• Radovic Ivana

  Department of Dental Materials and Restorative Dentistry, University of Siena

関連論文

• Surgical closure of patent ductus arteriosus reduces the cerebral tissue oxygenation index in preterm infants : a near-infrared spectroscopy and Doppler study
• Fatigue resistance and structural integrity of different types of fiber posts
• Non-linear Viscoelastic Finite Element Analysis of the Effect of the Length of Glass Fiber Posts on the Biomechanical Behaviour of Directly Restored Incisors and Surrounding Alveolar Bone
• Evaluation of the Skin Blood Flow Contribution to the Non-Invasive Measurement of Muscle Oxygenation by Near Infrared Spectroscopy
• Letter to the Editor, "Clinical Significance of Cerebral Oxygenation During Exercise in Patients With Coronary Artery Disease"(Letter to the Editor)
• Repair potential of a laboratory-processed nano-hybrid resin composite
• In vitro analysis of residual tooth structure of maxillary anterior teeth after different prosthetic finish line preparations for full-coverage single crowns
• Effect of different bonding procedures on micro-tensile bond strength between a fiber post and resin-based luting agents

スポンサーリンク