Interactive Strength between C60 Thin Film and Si(001) and Its Influence on Nano-Scaled Tribology
スポンサーリンク
概要
- 論文の詳細を見る
The influences of interactions between C60 thin films and Si substrates were investigated using atomic force microscopy (AFM). It was found that higher friction coefficient was obtained at the C60 domains formed on the H-terminated Si(001) substrate and lower ones on the Si(001)-2×1 substrate. Moreover, lowest friction coefficient was found for the C60 film on the Si(001)-2×1 remained after scratching. Therefore, it is thought that higher interactions between C60 and Si substrate caused lower friction coefficient of C60 thin film. The prepared substrate was examined by reflection high energy electron diffraction (RHEED), X-ray photoelectron spectroscopy (XPS), and Auger electron spectroscopy (AES).
- 社団法人 日本トライボロジー学会の論文
社団法人 日本トライボロジー学会 | 論文
- Influences of Film Deposition Condition on Friction of Diamond-Like Carbon Film: A Theoretical Investigation
- A Theoretical Study of Dynamic Behavior of Diphenyldisulphide Molecule on Fe Surface: Novel Ultra-Accelerated Quantum Chemical Molecular Dynamics Approach
- Friction and Wear Properties of Copper/Carbon/RB Ceramics Composite under Electrical Current
- Friction and Wear Properties of Copper/Carbon/RB Ceramics Composite Materials under Dry Condition
- Development of Acoustic Emission Viscosity Model for Measuring Engine Oil Viscosity Relationship with Engine Oil In-Service Age