Antiwear Performances of Dicarboxylic Acids in Vegetable Oils
スポンサーリンク
概要
- 論文の詳細を見る
This study deals with the evaluation of antiwear performance of the vegetable oils [soybean oil, corn oil, rapeseed oil, and sunflower oil] and their blends, containing varying amounts of acetone, and organic acids [oxalic acid, succinic acid, and adipic acid]. Four-ball tribometer was employed as the wear tester. Extensive optimization with respect to the test oil composition was performed in order to explore the conditions under which the test oil demonstrated superior antiwear performance. In all cases, the desired conditions were obtained under a narrow range of test oil composition. It was observed that under the constant applied load of 78 N, test duration of 1 h, and given oil viscosity, succinic acid was found to be the most effective antiwear additive, i.e., resulted in smaller wear scar diameter [WSD] among the employed acids in all the test oils. For example, at 0.02 wt % of the succinic acid loading, the relative wear [WSDacid-loaded oil / WSDacid-free oil] was found to be 0.53, 0.62, 0.65, and 0.67 for the soybean oil [vis., 35 cSt], corn oil [vis., 33 cSt], rapeseed oil [vis., 47 cSt], and sunflower oil [vis., 36 cSt], respectively. The values of of the relative wear obtained under similar conditions with the same oils in the presence of oxalic acid and adipic acid were on the higher side of those obtained with the succinic acid. Further work is in progress in order to formulate energy saving and high performance environmental friendly lubricants for a wide range of practical applications.
論文 | ランダム
- 焼成鉱の還元粉化機構の検討
- 35 焼成鉱の還元粉化現象(焼結・討論会, 製銑, 日本鉄鋼協会 第 101 回(春季)講演大会)
- 含 MgO 焼結鉱の溶融性状
- 36 含 MgO 焼結鉱の軟化溶融性状について(焼結・製銑基礎, 銑製, 日本鉄鋼協会 第 98 回(秋季)講演大会)
- 94 含 MgO 焼結鉱の高温性状について(焼結, 製銑・環境, 日本鉄鋼協会第 94 回(秋季)講演大会)