• Solid solution of the CeO2-YO1.5 system was studied extensively using X-ray diffraction, Raman spectroscopy and transmission electron microscopy. The results of X-ray diffraction analysis indicate that the solid solution was in fluorite structure over the compositional range 0-30mol%YO1.5. The results of Raman spectroscopy reveal that at 40-70mol%YO1.5, samples were fundamentally in fluorite structure but there was disorder formation that produced many satellite peaks in the X-ray diffraction patterns. At 90-100mol%YO1.5, the solid solution was in rare earth C-type structure.

• 社団法人粉体粉末冶金協会の論文

著者

• Ikuma Yasuro

  Kanagawa Inst. Of Tech.

• Ikuma Yasuro

  Kanagawa Institute Of Technology

• Nagasawa Shinya

  Kanagawa Institute of Technology

• Hayashi Nao

  Kanagawa Institute of Technology

• Kamiya Michiyo

  Kanagawa Institute of Technology

関連論文

• Temperature Change of Refractories during Exposure to Microwaves
• Effect of Heat-Assisting Material on Microwave Heating of Gamma Alumina
• Effect of Iron Oxide and Manganese Oxide Addition on Temperature of Aluminum Oxide and Silicon Oxide Mixture during Microwave Irradiation
• Temperature Change of Aluminum Oxide and Silicon Oxide Mixtures during Microwave Irradiation
• Crystal Structure of CeO2-YO1.5 System (特集 電池材料--SOFC(固体酸化物燃料電池)と二次電池材料)
• Temperature of Refractories during Exposure to Microwaves

スポンサーリンク