プラスチックフィルムの界面はく離解析: 非相溶樹脂の粒子径とボイド発現との関係
スポンサーリンク
概要
- 論文の詳細を見る
This study is concerned with the analysis of the relationship between the interfacial energy of a polymer and the micro voids that are formed by stretching the composite polymer sheet having incompatible particles in the matrix. The void formation caused by the interfacial delamination between Poly (ethylene terephthalate) (PET) and dispersed incompatible polymers of varying sizes was simulated by the finite element method (FEM) and compared with experimental measurements.The following results were obtained;(1) Experimentally, voids increased in size with increasing surface tension difference between PET and the incompatible polymers. The aspect ratio of the voids did not depend on particle size.(2) Theoretically, a decrease in the critical stress of delamination coincided with increasing the surface energy. The aspect ratio of the voids did not depend on particle size.(3) Interfacial tension obtained from this experiment was qualitatively related to the critical stress calculated from the numerical analysis of void formation.
- The Japan Society of Polymer Processing = プラスチック成形加工学会の論文
- 2001-06-20
The Japan Society of Polymer Processing = プラスチック成形加工学会 | 論文
- 絶縁用封止材として使われるエポキシ樹脂硬化反応の解析: 第3報 エポキシ樹脂の界面の段階的接着モデルによる応力-ひずみ解析
- プラスチック成形品のネック伝ぱ解析(1) : ポリブチレンテレフタレート成形品のネック伝ぱ挙動
- プラスチック成形品のネック伝ぱ解析(2): ポリブチレンテレフタレート成形品のネック挙動のひずみ速度依存性
- 絶縁用封止材として使われるエポキシ樹脂硬化反応の解析: 第2報 エポキシ樹脂の粘弾性構成則と界面完全接着モデルによる応力-ひずみ解析
- 絶縁用封止材として使われるエポキシ樹脂硬化反応の解析: 第4報 エポキシ樹脂の界面の破壊モデルによる応力-ひずみ解析