絶縁用封止材として使われるエポキシ樹脂硬化反応の解析: 第4報 エポキシ樹脂の界面の破壊モデルによる応力-ひずみ解析
スポンサーリンク
概要
- 論文の詳細を見る
Our previous report proposed a gradual adhesion model for the interface of epoxy resin used as an electric insulator. The model can deal with the flow and gelling of epoxy resin but it cannot deal with the fracture of the interface. In order to solve the fracture problem, two new fracture models are proposed for the epoxy resin interface.1) One model proposes that partial adhesion remains after the fracture of the interface of epoxy resin occurs. The calculated strain change using this model does not give good agreement with experimental values.2) Another model proposes that partial adhesion remains after the shrinkage strain from the curing reaction is released by the fracture of the interface. The calculated strain change from this model gives good agreement with experimental values.These results indicate that the weak adhesion region breaks away when the fracture of the epoxy resin interface occurs. The temperature distribution of the epoxy resin during the curing reaction does not change with the fracture of the interface. The internal stress of the epoxy resin goes up with the adhesion and goes down with the fracture of the epoxy resin interface.
- The Japan Society of Polymer Processing = プラスチック成形加工学会の論文
- 2003-06-20
The Japan Society of Polymer Processing = プラスチック成形加工学会 | 論文
- 絶縁用封止材として使われるエポキシ樹脂硬化反応の解析: 第3報 エポキシ樹脂の界面の段階的接着モデルによる応力-ひずみ解析
- プラスチック成形品のネック伝ぱ解析(1) : ポリブチレンテレフタレート成形品のネック伝ぱ挙動
- プラスチック成形品のネック伝ぱ解析(2): ポリブチレンテレフタレート成形品のネック挙動のひずみ速度依存性
- 絶縁用封止材として使われるエポキシ樹脂硬化反応の解析: 第2報 エポキシ樹脂の粘弾性構成則と界面完全接着モデルによる応力-ひずみ解析
- 絶縁用封止材として使われるエポキシ樹脂硬化反応の解析: 第4報 エポキシ樹脂の界面の破壊モデルによる応力-ひずみ解析