パルスYAGレーザによる溶接部の熱処理 : パルスYAGによるマイクロ補修溶接の研究(第2報)
スポンサーリンク
概要
- 論文の詳細を見る
This study describes laser heat treatment of alloy tool steels SKD11 using pulsed YAG laser. When filler metal SUJ2 is welded to base metal SKD11 which metal is material of rotary cutter, the hardness of weld metal become lower than that of the base metal. In order to improve the hardness of weld metal which become lower than that of the base metal after laser welding, heat treatments using an electric furnace and pulsed YAG laser were carried out after laser welding, then examined the variation of hardness of weld metal after heat treatments. The obtained results are as follows. In the heat treatment using an electric furnace, the hardness of weld metal which become low against the base metal after laser welding become higher than that of the base metal under the conditions of heat treatment holding temperature at 180℃ and holding time from 30s to 120s, then take out the weld metal from the electric furnace and cooling from furnace temperature to room temperature. In the heat treatment using pulsed YAG laser, after laser welding in succession laser beam radiate at the surface of weld metal, the hardness of weld metal which become low against the base metal after laser welding become the same hardness as the base metal under the conditions of holding temperature at 180℃ and holding time from 30s to 120s, then cooling to room temperature.
- 溶接学会の論文
- 2001-00-00
溶接学会 | 論文
- 研究者・技術者に必須の「効果的技術英文の組み立て方」 : テクニカル・ライティング練習張
- 補修溶接の採否の決定と施工上のポイント-2-圧力容器
- これからの溶接・接合技術の展開と提言
- 破壊靱性と継手破壊強度
- ものづくりを革新するレーザ溶接